The invention discloses a technology for controlling the heat treatment temperature of aluminium strip used for the shell of electrolytic capacitor. The aluminium material is made by continuous casting-rolling and cold rolling production method. The heat treatment process is that the metal temperature is controlled at 400 300 and the heat preservation time is 30 40 hours. In order to further improve the performance index of aluminium strip, the optimum metal temperature is controlled at 300 C for 40 hours. The aluminium strip for the shell of electrolytic capacitor is processed by continuous casting, rolling, cold rolling and heat treatment process, which reduces the production cost, simplifies the production process and facilitates the operation.
【技术实现步骤摘要】
一种铝带材热处理温度工艺控制技术
本专利技术涉及一种铝加工技术，特别是一种铝带材热处理温度工艺控制技术，适合于电解电容器外壳的加工处理。
技术介绍
目前，随着电子工业的飞速发展，电解电容器被广泛应用。电解电容器外壳用铝带材应具有良好的防爆性能及良好的深冲性能，既要求铝带材有好的抗拉强度，又要具有良好的延展性，其性能有良好的稳定性。一般要求铝材抗拉强度为8-10MPa，延伸率为15-40％，制耳率＜2％，无制耳或要求沿八个方向制耳。因此一般采取热轧-冷轧生产工艺。其生产成本较高。而普通连续铸轧-冷轧工艺生产带材的热处理技术不能满足要求。参考文献：1.变形铝及铝合金轧制板材GB/T3880；2.变形铝及铝合金化学成分分析取样方法GB/T17432；3.变形铝镁合金及其合金加工制品拉伸试验用试样GB/T16865；4.镁及铝镁合金专业手册。
技术实现思路
本专利技术所要解决的问题在于，克服现有铝带材生产工艺的不足，提供了一种铝带材热处理温度工艺控制技术。该技术不仅热处理工艺合理，而且降低生产成本，使其生产工艺简单化，便于操作。本专利技术采用的技术方案是：采用连续铸轧-冷轧生产制作方法制作的铝材料，其热处理工艺为：金属温度控制在400℃-300℃，保温30-40小时。为了进一步提高铝带材的性能指标，最佳金属温度控制在300℃，保温40小时。通过实施本专利技术，具有以下特点：1.采用连续铸轧冷轧工艺生产电解电容器外壳用带材以降低生产成本。2.在熔炼过程中通过铁、硅等成分的调整来形成良好的抗卡强度与延伸率。3.通过对最终产品热处理工艺调整最终产品性能。本专利技术的有益效果...
【技术保护点】
1.一种铝带材热处理温度工艺控制技术，其特征在于：采用连续铸轧冷轧生产制作方法制作的铝材料，，其热处理工艺为：金属温度控制在260℃‑300℃，保温30‑40小时。
【技术特征摘要】
1.一种铝带材热处理温度工艺控制技术，其特征在于：采用连续铸轧冷轧生产制作方法制作的铝材料，，其热处理工艺为：金属温度控制在260℃-30...