The invention belongs to the technical field of titanium alloys, and discloses a preparation method of medical titanium alloy Ti 13Nb 13Zr ingot, in which fine particles of sponge titanium and refractory metal Nb powder are selected; according to the proportion of the weight percentage of sponge titanium and refractory metal Nb powder of 2-4:1, the sponge zirconium is evenly mixed by mechanical stirring through a mixer, then added into the electrode block, and pressed by an oil press. Ti alloy Ti_ 13Nb_ 13Zr ingot was produced by vacuum consumable arc furnace. The invention greatly reduces the production cost of titanium alloy Ti 13Nb 13Zr ingot. The produced titanium alloy Ti 13Nb 13Zr ingot meets the requirements of GB/T3620.1 2016 standard by testing its chemical composition, has no segregation and inclusion of refractory metal Nb element, and has good metallurgical quality.
【技术实现步骤摘要】
一种医用钛合金Ti-13Nb-13Zr铸锭及其制备方法
本专利技术属于钛合金
，尤其涉及一种医用钛合金Ti-13Nb-13Zr铸锭制备方法。
技术介绍
目前，业内常用的现有技术是这样的：钛的熔点1668℃，铌的熔点2468℃，二者差别较大，含有Nb的钛合金熔炼时通常将Nb以中间合金Ti-40～50％Nb形式加入Ti-13Nb-13Zr合金中，由于需要加入高含量难熔Nb金属的中间合金，容易在铸锭中产生中间合金不熔块形成严重的冶金缺陷；另外高难熔金属含量的中间合金制备工艺复杂、价格较高，而且破碎困难。含难熔金属Nb的钛合金具有低弹性模量、高强度、生物和力学相容性好等特点，是人体硬组织替代外科植入件的理想材料。含难熔金属Nb的钛合金，铸锭中难熔金属元素Nb均匀化分布是保证铸锭质量的关键。难熔Nb金属与钛粉以粉末法加入，钛粉的添加易引起铸锭氧含量控制困难，而且加入钛粉，使合金的成本增高且工艺复杂。综上所述，现有技术存在的问题是：(1)现有技术中，由于需要加入高含量难熔Nb金属的中间合金(Ti-40～50％Nb)，容易在铸锭中产生中间合金不熔块形成严重的冶金缺陷。(2...
【技术保护点】
1.一种医用钛合金Ti‑13Nb‑13Zr铸锭，其特征在于，所述种医用钛合金Ti‑13Nb‑13Zr铸锭由铌、锆和钛组成，按照重量百分比铌12.5％‑14％，锆12.5％‑14％，余量为钛及不可避免的杂质。
【技术特征摘要】
1.一种医用钛合金Ti-13Nb-13Zr铸锭，其特征在于，所述种医用钛合金Ti-13Nb-13Zr铸锭由铌、锆和钛组成，按照重量百分比铌12.5％-14％，锆12.5％-14％，余量为钛及不可避免的杂质。2.一种如权利要求1所述医用钛合金Ti-13Nb-13Zr铸锭的制备方法，其特征在于，所述的医用钛合金Ti13Nb13Zr铸锭的制备方法包括以下步骤：步骤一：选取细颗粒海绵钛和难熔金属Nb粉末，备用；步骤二：按海绵钛与难熔金属Nb粉末的重量百分比为2～4∶1的比例，通过混合机进行机械搅拌混...
【专利技术属性】
技术研发人员：陈杜娟，曹继敏，罗乾伟，樊亚军，贺峰，曹依玮，王戈，张温馨，
申请(专利权)人：西安圣泰金属材料有限公司，
类型：发明
国别省市：陕西,61
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。