The invention discloses a preparation method of porous carbon material derived from biomass tar. The steps are simple. The biomass tar waste is converted into porous carbon material with high specific surface area, narrow pore size distribution and double-layer characteristics. The porous carbon material can be used as carbon electrode of supercapacitor with excellent electrochemical performance, high value of tar waste is recycled, and the traditional activation method is solved. It is difficult to prepare porous carbon materials for carbon electrodes of supercapacitors, which have stricter requirements on surface area and pore structure. It also provides a new method for resourceful utilization of existing biomass tar.
【技术实现步骤摘要】
一种生物质焦油衍生多孔碳材料的制备方法
：本专利技术涉及功能材料领域，具体涉及一种生物质焦油衍生多孔碳材料的制备方法。
技术介绍
：我国作为农业大国，拥有巨量的生物质资源，这为生物质气化技术的发展提供了良好的基础，但是气化过程中产生的生物质焦油是制约气化技术快速发展的主要因素。目前对焦油的净化处理方法主要是热化学转化法，然而其存在着高温要求高(＞1000℃)且产物附加值低等缺陷。多孔碳材料是指具有不同孔道结构的碳材料，包括活性碳、碳分子筛等，按照其孔径大小，多孔碳材料中的孔结构可以分为如下3种：微孔(孔径＜2nm)，介孔(2nm＜孔径＜50nm)，大孔(孔径＞50nm)。多孔碳材料因其具有高度发达的内表面和孔隙结构,作为吸附剂、电极材料和催化剂载体广泛应用于气体的吸附分离与净化、电化学及催化等领域。超级电容器，作为一种介于传统电容器和电池之间的新型的储能器件，近年来发展十分迅速，这也对作为电极的碳材料提出更高的性能要求，然而传统的活化方法难以制备出对比表面积、孔结构有更严格要求的多孔碳材料。因此,近年来开发高比表面积、孔径分布狭窄的多孔碳材料已成为一项国内外储能产...
【技术保护点】
1.一种生物质焦油衍生多孔碳材料的制备方法，其特征在于，该方法包括以下步骤：(1)将Y型分子筛与生物质焦油以≥2的质量比置于石英舟中，石英舟置于管式炉中央，通氮气排尽空气，升温至600～800℃进行反应，保持反应温度20‑60min，升温速率为5‑15℃/min，反应结束后自然冷却至室温；(2)将步骤(1)得到的产物浸于15‑20wt％的氢氟酸溶液，搅拌20‑24h，布氏漏斗中进行抽滤，滤渣用蒸馏水冲洗至中性；(3)将步骤(2)得到的滤渣转移至17‑18wt％的盐酸溶液，搅拌20‑24h，抽滤洗涤至中性，真空干燥即得具有高比表面积和窄的孔径分布且具有双电层特性的多孔碳材料；...
【技术特征摘要】
1.一种生物质焦油衍生多孔碳材料的制备方法，其特征在于，该方法包括以下步骤：(1)将Y型分子筛与生物质焦油以≥2的质量比置于石英舟中，石英舟置于管式炉中央，通氮气排尽空气，升温至600～800℃进行反应，保持反应温度20-60min，升温速率为5-15℃/min，反应结束后自然冷却至室温；(2)将步骤(1)得到的产物浸于15-20wt％的氢氟酸溶液，搅拌20-24h，布氏漏斗中进行抽滤，滤渣用蒸...
【专利技术属性】
技术研发人员：袁浩然，李德念，张贤，
申请(专利权)人：中国科学院广州能源研究所，
类型：发明
国别省市：广东,44
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。