The invention belongs to the field of welding technology, and discloses a double-sided double-arc perforation welding method based on K_TIG. The method places K_TIG torch and GTAW torch on opposite sides of butt seam of welded parts, K_TIG torch is connected with negative electrode of welding machine power supply, GTAW torch is connected with positive electrode of welding machine power source, K_TIG torch and GTAW torch are simultaneously welded on the same position of butt seam of welded parts. The nozzle of K_TIG welding torch is perpendicular to the welding position of the butt seam of the welded piece, so that the welding arc passes through the weld hole. The invention combines the original K_TIG process with the double-sided double arc piercing welding process, solves the problem that K_TIG welding can only stabilize the piercing welding of the workpiece with low thermal conductivity, greatly reduces the piercing current, and also reduces the deformation degree of the workpiece through the double-sided arc welding process.
【技术实现步骤摘要】
基于K-TIG的双面双弧穿孔焊接方法
本专利技术涉及焊接
，具体的说，是涉及一种基于K-TIG的焊接方法。
技术介绍
K-TIG(锁孔高效熔深氩弧焊焊枪)是一种基于传统TIG焊枪，通过水冷钨极产生阴极收缩效应，配合较大焊接电流的新型穿孔焊接工艺方法。经过大量的工艺试验证明：K-TIG焊接工艺适合于焊接低热导率的金属材料，但由于采用的自由电弧平均能量密度低，小孔稳定性随工件热导率的增加而恶化。在焊接中厚板时，电弧收缩程度不够，不利于形成稳定的穿透小孔，所以K-TIG焊接工艺得到合格焊缝的工艺窗口较小。因此，需要进一步改进K-TIG焊接工艺，能够有效地调控焊接电弧形态，保证小孔的稳定性。改善电弧特性，提高其能量密度，能够提高穿孔稳定性。目前尝试了两种方案：一种是通过尖角磁场收缩电弧，由于外加环形磁场能够沿电弧周长对电弧产生作用力，因此将环形磁场加载在K-TIG电弧上，通过改变磁场的强度和分布，能够调节电弧的形态和电弧特性，通过施加双尖角磁场，电弧的剖面由圆形变为椭圆形；同时持续通冷却水并始终充满装置的腔体，对永磁铁进行持续降温。经过实验表明：优化磁场后，穿孔焊接...
【技术保护点】
1.一种基于K‑TIG的双面双弧穿孔焊接方法，其特征在于，该方法将K‑TIG焊枪和GTAW焊枪相对地置于被焊件对接缝的两侧，所述K‑TIG焊枪与焊机电源的负极相连，所述GTAW焊枪与所述焊机电源的正极相连，所述K‑TIG焊枪和所述GTAW焊枪同时对被焊件对接缝进行焊接，其中所述K‑TIG焊枪的喷头垂直于被焊件对接缝的焊接位置，使焊接电弧穿过焊缝小孔。
【技术特征摘要】
1.一种基于K-TIG的双面双弧穿孔焊接方法，其特征在于，该方法将K-TIG焊枪和GTAW焊枪相对地置于被焊件对接缝的两侧，所述K-TIG焊枪与焊机电源的负极相连，所述GTAW焊枪与所述焊机电源的正极相连，所述K-TIG焊枪和所述GTAW焊枪同时对被焊件对接缝进行焊接，其中所述K-TIG焊枪的喷头垂直于被焊件对接缝的焊接位置，使焊接电弧穿过焊缝小孔。2.根据权利要求1所述的一种基于K-TIG的细口径管道双面...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。