The invention relates to a shrinkage die for reducing the tendency of shrinkage instability, which belongs to the technical field of light alloy plastic forming. The invention mainly solves the technical problems existing in the existing shrinkage die that the lower half of the blank is easy to be unstable, the parts are easy to be scrapped and the materials are wasted. The technical scheme adopted by the invention is: a shrinkage die for reducing the tendency of shrinkage instability. On the basis of the busbar of the inner wall of the shrinkage die, a plurality of transverse annular grooves are arranged on the inner wall of the shrinkage die. The ratio of the height H of the inner wall of the shrinkage die to the height L of the transverse annular groove is H/L, the ratio of the straight to the air is 1:1:1.6, and the depth t of the transverse annular groove is 0.5-3 mm. The invention is suitable for various non-ferrous metals and ferrous metals, and has a wide application range.
【技术实现步骤摘要】
一种降低缩口失稳倾向的缩口凹模
本专利技术涉及一种降低缩口失稳倾向的缩口凹模，它属于轻合金塑性成形
技术介绍
在传统的缩口工艺中，缩口凹模内壁的母线形式基本上分为两种情况，一种是缩口凹模母线为直线(见图1)，另一种缩口凹模母线为曲线(见图2)。若缩口凹模母线形式为直线，因为凹模内壁与毛坯已完成的缩口部分面积会100％接触，因此随着缩口过程进行，凹模内壁与毛坯接触面积会越来越大，这样压力机通过凹模传递给毛坯筒的轴向压力F轴越来越大，毛坯筒下端部发生失稳的可能性就越来越大。因此，现有缩口工艺只能进行局部缩口不能进行整体缩口，只能进行缩口系数大于0.73的变形，不能进行缩口系数小于0.73的变形。为解决上述技术问题，申请人把缩口凹模母线形式变为曲线，随着缩口过程进行，毛坯已完成的缩口部分母线微观近似连续折线，折线尖点与凹模内壁接触，其余不接触，这样，毛坯与凹模内壁的接触面积相对于直线母线来说可减少50％～60％，接触面积的减少使压力机传递给毛坯筒下端部的轴向压力F轴减小，降低毛坯筒壁的失稳倾向。虽然缩口凹模母线形式变为曲线，可以降低毛坯筒壁的失稳倾向。但若要进...
【技术保护点】
1.一种降低缩口失稳倾向的缩口凹模，其特征在于：在缩口凹模内壁母线的基础上，在缩口凹模内壁设置多道横向环状沟槽，缩口凹模内壁间隔斜壁高度H与横向环状沟槽高度L的比值为直空比H/L，直空比为1:1～1:1.6，横向环状沟槽的深度t为0.5～3mm。
【技术特征摘要】
1.一种降低缩口失稳倾向的缩口凹模，其特征在于：在缩口凹模内壁母线的基础上，在缩口凹模内壁设置多道横向环状沟槽，缩口凹模内壁间隔斜壁高度H与横向环状沟槽高度L的比值为直空比H/L，直空比为1:1～1:1.6，横向环状沟槽的深度t为0.5～3m...
【专利技术属性】
技术研发人员：程眉，李国俊，吴昂，张治民，王强，郭为民，
申请(专利权)人：中北大学，
类型：发明
国别省市：山西,14
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。