The invention discloses a method for increasing the capacity of 1.55V lithium titanate batteries by solid state reaction. The preparation method is as follows: taking raw materials titanium dioxide, lithium carbonate and yttrium oxide in proportion, after ball milling and grinding or ball milling, the mixed powder is heated to 700 900 degrees Celsius in high temperature furnace in air atmosphere, sintered for 10 15h, and the synthesis has a component. The sub-formula is Li0.99Y0.01Li1/3Ti5/3O4 lithium titanate powder, washed with deionized water and dried. The invention adds yttrium oxide to titanium dioxide and lithium carbonate, and through designing the ratio of three raw materials, the capacity of 1.55V lithium titanate battery synthesized by solid state reaction is 244 mAh/g.
【技术实现步骤摘要】
一种通过固相反应提高1.55V钛酸锂电池容量的方法
本专利技术涉及钛酸锂电池，尤其是提供一种提高1.55V钛酸锂电池容量的方法。
技术介绍
20世纪九十年代，钛酸锂Li4Ti5O12作为新型锂电池的负极材料出现，由于它的高安全性、高稳定性、长寿命和绿色环保的特点能而受到重视。就目前所使用的钛酸锂电池，是以钛酸锂作为负极材料代替石墨，可与锰酸锂、三元材料或磷酸铁锂等正极材料组成2.4V或1.9V的锂离子二次电池。钛酸锂电池优势明显，其不足之处也很明显，比如能量密度相对较低，续航能力弱，这很大程度上由单体电池的电压决定，经测试，对锂电位1.5V，钛酸锂的克容量理论上为174mAh/g，只有传统石墨负极材料的一半，这对电池容量要求较高的场合，钛酸锂电池就没有太大的优势，因此低容量限制了钛酸锂电池的用量，这是该技术路线的客观短板。现有公开的文献中也有提高钛酸锂电池容量的方法，但大都是通过添加化合物或者硅、碳元素复合或者改性的方法来实现的，比如中国专利申请号201310219768.3公开的一种高容量钛酸锂负极材料的制备方法；中国专利申请号201510331370.8公开的...
【技术保护点】
1.一种通过固相反应提高1.55V钛酸锂电池容量的方法,其特征在于，制备方法为：取原料二氧化钛、碳酸锂和氧化钇，其中Li：Ti:Y的摩尔比为1.323:1.666:0.01，上述三种原料经过研磨粒度小于50nm混合均匀后，将混合粉末置于空气气氛中高温炉中升温至烧结温度700‑900摄氏度，进行保温烧结10‑15h，合成具有分子式为Li0.99Y0.01Li1/3Ti5/3O4的钛酸锂粉末，再用去离子水洗涤，烘干即可。
【技术特征摘要】
1.一种通过固相反应提高1.55V钛酸锂电池容量的方法,其特征在于，制备方法为：取原料二氧化钛、碳酸锂和氧化钇，其中Li：Ti:Y的摩尔比为1.323:1.666:0.01，上述三种原料经过研磨粒度小于50nm混合均匀后，将混合粉末置于空气气氛中高温炉中升温至烧结温度7...
【专利技术属性】
技术研发人员：谷亦杰，潘铭，刘洪权，
申请(专利权)人：安徽赛尔新能源科技有限公司，
类型：发明
国别省市：安徽,34