铸膜液、超滤膜、反渗透复合膜或者纳滤复合膜制造技术

本发明专利技术提供了铸膜液、超滤膜以及制备超滤膜的方法。其中，铸膜液包括：聚砜、组合添加剂、非溶剂以及溶剂；其中所述组合添加剂包括聚乙烯吡咯烷酮和醇，所述聚乙烯吡咯烷酮的相对分子质量不小于20万且不大于150万。由此，该铸膜液的粘度较为合适，铸膜液中几乎没有气泡，利于成膜。

Cast Membrane Liquid, Ultrafiltration Membrane, Reverse Osmosis Composite Membrane or Nanofiltration Composite Membrane

The invention provides a casting solution, an ultrafiltration membrane and a method for preparing an ultrafiltration membrane. The casting solution includes polysulfone, combination additive, non-solvent and solvent, and the combination additive includes polyvinyl pyrrolidone and alcohol, and the relative molecular weight of the polyvinyl pyrrolidone is not less than 200,000 and not more than 1.5 million. As a result, the viscosity of the casting solution is more appropriate, and there are almost no bubbles in the casting solution, which is conducive to film formation.

【技术实现步骤摘要】
铸膜液、超滤膜、反渗透复合膜或者纳滤复合膜
本专利技术涉及制膜
，具体的，涉及铸膜液、超滤膜、反渗透复合膜或者纳滤复合膜，更具体的，涉及铸膜液、超滤膜、反渗透复合膜或者纳滤复合膜、纯水或净水供应方法以及纯水或净水供应装置。
技术介绍
膜分离技术主要分为反渗透(RO)、纳滤(NF)、超滤(UF)、微滤(MF)四种分离技术，其中，反渗透技术已广泛应用于海水和苦咸水淡化、纯水制备、工业用水处理、废水处理，以及医药、化工和食品等工业料液的处理和浓缩等过程。目前，反渗透过程的操作压力较高，苦咸水淡化操作压力一般为1.5-2.0MPa，海水淡化的操作压力将大于2.0MPa，纳滤复合膜的操作压力也在0.5MPa以上。所以用于反渗透技术的反渗透复合膜和纳滤复合膜中支撑基膜的性质至关重要。
技术实现思路
本专利技术的一个目的在于提出一种铸膜液，利用该铸膜液制备得到的超滤膜具备海绵状孔结构，其水通量较高而且耐压性较高，进而利用该超滤膜制备得到的反渗透复合膜或纳滤复合膜的耐压性好、可以在较高的压力下使用，而且水通量和截留率性能较高。在本专利技术的一个方面，本专利技术提供了一种铸膜液。根据本专利技术的实施本文档来自技高网...

【技术保护点】
1.一种铸膜液，其特征在于，包括：聚砜；组合添加剂，所述组合添加剂包括聚乙烯吡咯烷酮和醇；非溶剂；以及溶剂，其中，所述聚乙烯吡咯烷酮的相对分子质量不小于20万且不大于150万。

【技术特征摘要】
1.一种铸膜液，其特征在于，包括：聚砜；组合添加剂，所述组合添加剂包括聚乙烯吡咯烷酮和醇；非溶剂；以及溶剂，其中，所述聚乙烯吡咯烷酮的相对分子质量不小于20万且不大于150万。2.根据权利要求1所述的铸膜液，其特征在于，所述聚乙烯吡咯烷酮选自聚乙烯吡咯烷酮K60、聚乙烯吡咯烷酮K85和聚乙烯吡咯烷酮K90中的至少之一；任选的，所述聚乙烯吡咯烷酮和醇的质量比为1-5：1。3.根据权利要求1所述的铸膜液，其特征在于，所述非溶剂包括水、丙酮、丁酮、柠檬酸、醋酸和磷酸中的至少之一；所述醇包括丙醇、乙醇、乙二醇和正丁醇中的至少之一；所述溶剂包括二甲基甲酰胺、二甲基乙酰胺、N-甲基吡咯烷酮、二甲基亚砜和氯仿中的至少之一。4.根据权利要求1-3任一项所述的铸膜液，其特征在于，包括：15～30重量份的所述聚砜；1～15重量份的所述组合添加剂；0.5～5重量份的所述非溶剂；50～83.5重量份的所...

【专利技术属性】
技术研发人员：柳艳敏，孟祥钦，郭宇，丁宇，孙蒙蒙，陈月霞，赵伟建，
申请(专利权)人：中国乐凯集团有限公司，
类型：发明
国别省市：河北,13