The invention discloses a composite material prepared by biomass combustion slagging and a preparation method, which is mainly made of the following weight parts of raw materials: biomass combustion slagging 20 50 parts; recycled plastics 30 60 parts; magnesium hydroxide flame retardant 10 30 parts; lubricant 3 5 parts. The present invention takes biomass combustion furnace slagging and recycling plastics as the main raw material, has low cost, simple and feasible production process; the material has good flame retardant performance and mechanical strength, and is environmentally friendly, pollution-free, recyclable, turning waste into treasure, and to a certain extent is conducive to alleviating environmental pollution and resource shortage.
【技术实现步骤摘要】
一种以生物质燃烧结渣为原料的复合材料及其制备方法
本专利技术涉及一种新型复合材料及其制备方法，具体涉及一种以生物质燃烧结渣为原料的复合材料及其制备方法。属于新型复合材料领域。
技术介绍
我国是农业大国，每年大约产生9亿吨农作物秸秆，另外还有2.7亿吨林业及木材加工废弃物，大体相当于2.5亿吨标准煤。仅山东省每年农业大约产生7000万吨的农作物秸秆，其中以小麦秸秆、玉米秸秆、棉花秸秆为主，除此之外林业及木材加工废弃物也有大约2000万吨。目前仅用于畜牧业、造纸业、板材加工业、以及秸秆还田的农业废弃物仅占总量的一半，其余大部分被农户当作柴薪焚烧。由于社会经济的发展，农村劳动力的转移，化肥等肥料的使用以及能源利用方式的改善农林废弃物更是出现了过剩现象。再者由于缺乏专业知识和有效利用方法，农作物收获之后，农民一般将秸秆就地焚烧，不仅造成污染环境还严重浪费了资源，甚者发生火灾造成安全隐患。若是将农作物秸秆放置田间闲置不用，不仅会大量占用土地，久置不用还会发生腐烂滋生细菌引来蝇虫，影响农副产品质量以及居民生活健康。因此，农林生物质资源的合理有效利用已经迫在眉睫。作为农林生物质...
【技术保护点】
1.一种利用生物质燃烧结渣制备的复合材料，其特征在于，主要由如下重量份的原料制成：生物质燃烧结渣20‑40份；回收塑料37‑57份；氢氧化镁阻燃剂20份；润滑剂3份。
【技术特征摘要】
1.一种利用生物质燃烧结渣制备的复合材料，其特征在于，主要由如下重量份的原料制成：生物质燃烧结渣20-40份；回收塑料37-57份；氢氧化镁阻燃剂20份；润滑剂3份。2.根据权利要求1所述的一种利用生物质燃烧结渣制备的复合材料，其特征在于，所述生物质燃烧结渣为农林生物质燃烧后产生的结渣。3.根据权利要求2所述的一种利用生物质燃烧结渣制备的复合材料，其特征在于，所述农林生物质包括玉米秸秆成型燃料。4.根据权利要求1所述的一种利用生物质燃烧结渣制备的复合材料，其特征在于，所述回收塑料为聚乙烯或聚丙烯等聚烯烃塑料。5.根据权利要求1所述的一种利用生物质燃烧结渣制备的复合材料，其特征在于，所述氢氧化镁阻燃剂是一种添加型环保阻燃剂，呈白色粉末状，粒径为60-80目。6.根据权利要求1所述的一种利用生物质燃烧结渣制备的复合材料，其特征在于，所述润滑剂是一种高填充体系的高效润滑剂，外观是粒状物，滴落点67-77℃，比重1.005g/cm3。7.权利要求1～6任一项所述复合材料的制备方法，其特征在于，包括以...
【专利技术属性】
技术研发人员：易维明，蔡红珍，张庆法，林晓娜，柳善建，
申请(专利权)人：山东理工大学，
类型：发明
国别省市：山东,37
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。