The invention belongs to the field of functional textiles, in particular to a conductive and washable graphene/silver composite cotton fabric, comprising a cotton fabric matrix, a graphene monolayer attached to the cotton fabric matrix and a silver film attached to the graphene monolayer, the cotton fabric matrix is composed of cotton fabric fibers, the graphene monolayer is composed of graphene nanosheets, and the graphene nanosheets are attached. The silver film is composed of silver particles which are embedded in graphene nanosheets and filled in the gap between graphene nanosheets. The preparation method is that cotton fabric is plasma treated, graphene oxide is adhered to and reduced, and finally conductive graphene/silver composite cotton fabric is obtained by magnetron sputtering silver target. The conductivity and washability of the composite cotton fabric of the invention are greatly improved, the quality of the cotton fabric is improved, the application field is expanded, and the commercial value of the composite cotton fabric is enhanced.
【技术实现步骤摘要】
一种导电耐水洗石墨烯/银复合棉织物及其制备方法
本专利技术属于功能纺织品领域,具体涉及一种导电耐水洗石墨烯/银复合棉织物及其制备方法。
技术介绍
随着材料科学和纳米技术等新兴学科的发展,新材料和纳米技术等成为21世纪的研究热点,并被广泛应用于电子信息、生物医学、机械制造等领域。由于各学科的相互交叉与渗透,将导电新材料与纺织面料相结合制备具有优良导电性能的功能纺织品已成为纺织领域的研究热潮。石墨烯自2004年被A.Geim和K.Novoselov发现以来,由于其独特的二维平面结构和优越的光学、电学特性等优点,成为近几年的研究热点之一,其优异的透光率、电子迁移率和导电率、力学性能和机械延展性、良好的热稳定性与化学稳定性,使其在光电子器件领域具有广泛的应用前景。然而石墨烯不易分散加上普通浸渍带来的易脱落问题,使其在织物上的运用较少,为了提导电织物的质量,拓展导电织物的应用领域,满足实际应用的需求,制备导电耐水洗的纺织材料仍是当今研究的热点。
技术实现思路
本专利技术提供一种导电耐水洗石墨烯/银复合棉织物,该复合棉织物克服现有石墨烯复合织物导电性不强及不耐水洗的缺陷,增强石墨烯与棉织物的界面粘结强度,导电性大幅提升,耐水洗强度增强,提高复合棉织物的质量,扩展其应用领域,提升商业价值。本专利技术还提供一种导电耐水洗石墨烯/银复合棉织物的制备方法,该方法简单易控,解决简单浸渍导致的导电性不强及不耐水洗的缺陷。本专利技术的技术方案为,一种导电耐水洗石墨烯/银复合棉织物,包括棉织物基体、附着在棉织物基体上的石墨烯单片层和附着在石墨烯单片层上的银薄膜,所述棉织物基体由棉织物纤维 ...
【技术保护点】
1.一种导电耐水洗石墨烯/银复合棉织物,其特征在于,包括棉织物基体、附着在棉织物基体上的石墨烯单片层和附着在石墨烯单片层上的银薄膜,所述棉织物基体由棉织物纤维构成;所述石墨烯单片层由石墨烯纳米片组成,石墨烯纳米片附着在棉织物纤维表面,并在棉织物纤维间穿插延伸;所述银薄膜由银颗粒组成,所述银颗粒嵌入石墨烯纳米片并填充石墨烯纳米片间间隙。
【技术特征摘要】
1.一种导电耐水洗石墨烯/银复合棉织物,其特征在于,包括棉织物基体、附着在棉织物基体上的石墨烯单片层和附着在石墨烯单片层上的银薄膜,所述棉织物基体由棉织物纤维构成;所述石墨烯单片层由石墨烯纳米片组成,石墨烯纳米片附着在棉织物纤维表面,并在棉织物纤维间穿插延伸;所述银薄膜由银颗粒组成,所述银颗粒嵌入石墨烯纳米片并填充石墨烯纳米片间间隙。2.根据权利要求1所述的导电耐水洗石墨烯/银复合棉织物,其特征在于,所述银薄膜的厚度为600~1500nm。3.根据权利要求1所述的导电耐水洗石墨烯/银复合棉织物,其特征在于,所述银薄膜呈网状分布。4.权利要求1-3任一项所述导电耐水洗石墨烯/银复合棉织物的制备方法,其特征在于,步骤包括:(1)棉织物用含碱有机溶剂清洗后,进行低压真空等离子体修饰;(2)将经等离子修饰的棉织物浸入氧化石墨烯水溶液中,经恒温浸渍的“一浸一轧”得到表面附着氧化石墨烯单片层的棉织物;(3)表面附着氧化石墨烯单片层的棉织物浸入还原剂水溶液还原,并干燥得到表面附着石墨烯单片层的棉织物;(4)以表面附着石墨烯单片层的棉织物为基底,以银为靶材,抽真空后,充入不活泼气体并保持基底旋转的情况下,进行磁控溅射,在棉织物表面附着的石墨烯单片层上附着银薄膜,得到石墨烯/银复合棉织物。5.根据权利要求4所述的制备方法,其特征在于,步骤(4)中,表面附着石墨烯单片层的棉织物表面固定覆盖有格栅。6.根据权利要求4所述的制备方法,其特征在于,步骤(1)中,所述碱为氢氧化钠、氢...
【专利技术属性】
技术研发人员:辛斌杰,何姗,陈卓明,杨盈,姜宇,肖雅倩,孟娜,
申请(专利权)人:上海工程技术大学,
类型:发明
国别省市:上海,31
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。