一种Fe-Al涂层的制备方法技术

本发明专利技术提供了一种Fe‑Al涂层的制备方法。本发明专利技术是在非水溶液中对活化后的基体进行原位电镀，得到的镀层组织致密、结晶细致、具有较高的位错密度。经过热处理可得到渐变式成分、结构的Fe‑Al涂层，涂层与基体结合牢靠，且分布均匀。根据实施例的记载，本发明专利技术所述的制备方法制备得到的Fe‑Al涂层的维氏显微硬度为6.15HV～7.48HV。

A Fabrication Method of Fe-Al Coating

The invention provides a preparation method of Fe_Al coating. The present invention is in-situ electroplating of activated matrix in non-aqueous solution, and the obtained coating has compact structure, fine crystallization and high dislocation density. After heat treatment, Fe_Al coatings with graded composition and structure can be obtained. The coatings are firmly bonded with the matrix and uniformly distributed. According to the description of the embodiment, the Vickers microhardness of the Fe_Al coating prepared by the preparation method of the present invention is 6.15HV~7.48HV.

【技术实现步骤摘要】
一种Fe-Al涂层的制备方法
本专利技术涉及Fe结构材料表面防护
，尤其涉及一种Fe-Al涂层的制备方法。
技术介绍
Fe-Al是一种金属间化合物，具有良好的高温抗氧化、抗硫化及耐腐蚀性能、密度小、成本低、高温强度和比强度高等优点，同时，作为环境友好材料，不会对环境产生污染，在近年来受到普遍的重视和研究。目前，Fe-Al涂层的制备方法有热浸镀法、粉末埋渗法、料浆法、气相法和热喷涂法等。但利用上述制备方法会存在制备过程中处理温度过高导致基体的高温强度和抗蠕变性能下降的问题。也就是说，现有技术中还没有一种能够满足基体高温强度和抗蠕变性能不会下降的方法。
技术实现思路
本专利技术的目的在于提供一种制备Fe-Al涂层的方法，且得到的Fe-Al涂层中基体的高温强度和抗蠕变性能不会下降。为了实现上述专利技术目的，本专利技术提供以下技术方案：本专利技术提供了一种Fe-Al涂层的制备方法，包括以下步骤：将AlCl3和有机盐混合，得到AlCl3非水溶液；以铁基镀件为阳极、铝为阴极、所述AlCl3非水溶液为电解质，对所述铁基镀件进行活化，得到活化铁基镀件；以铝为阳极、所述活化铁基镀件为阴极、所述AlC本文档来自技高网...

【技术保护点】
1.一种Fe‑Al涂层的制备方法，包括以下步骤：将AlCl3和有机盐混合，得到AlCl3非水溶液；以铁基镀件为阳极、铝为阴极、所述AlCl3非水溶液为电解质，对所述铁基镀件进行活化，得到活化铁基镀件；以铝为阳极、所述活化铁基镀件为阴极、所述AlCl3非水溶液为电解质，进行电镀铝，在所述活化铁基镀件的表面形成铝镀层，得到镀铝初坯；将所述镀铝初坯进行热处理，在所述铁基镀件的表面形成Fe‑Al涂层。

【技术特征摘要】
1.一种Fe-Al涂层的制备方法，包括以下步骤：将AlCl3和有机盐混合，得到AlCl3非水溶液；以铁基镀件为阳极、铝为阴极、所述AlCl3非水溶液为电解质，对所述铁基镀件进行活化，得到活化铁基镀件；以铝为阳极、所述活化铁基镀件为阴极、所述AlCl3非水溶液为电解质，进行电镀铝，在所述活化铁基镀件的表面形成铝镀层，得到镀铝初坯；将所述镀铝初坯进行热处理，在所述铁基镀件的表面形成Fe-Al涂层。2.如权利要求1所述的制备方法，其特征在于，所述有机盐为卤化烷基吡啶、卤化烷基咪唑和卤化烷芳基铵盐中的一种或几种。3.如权利要求1或2所述的制备方法，其特征在于，所述AlCl3和有机盐的摩尔比为(1.5～2.0)：1。4.如权利要求1所述的制备方法，其特...

【专利技术属性】
技术研发人员：杨飞龙，张桂凯，向鑫，刘浪，唐金强，陈长安，唐涛，
申请(专利权)人：中国工程物理研究院材料研究所，
类型：发明
国别省市：四川,51