The invention relates to a rust preventive cutting fluid for iron casting and a preparation method thereof, which are composed of various components of the following quality parts: the pentaerythritol ester 3, 8 parts, two phenyl two octyl ester 3, 6 parts, oleic acid epoxy ester 2 2 4 parts, two polyacid 1 1 2 parts, ultrafine aluminum silicate 2 parts, acrylic emulsion emulsion parts, deionized water extract, antioxidant and preservative. 1 3 copies of antirust agent. The anti-rust cutting fluid for cast iron processing is specially designed for cast iron processing, has ideal cooling and lubricating effects, and can avoid the corrosive effect of a large amount of smoke and dust on processing tools, provides processing accuracy and efficiency, and is very conducive to use in the process of cast iron processing.
【技术实现步骤摘要】
一种铸铁加工防锈切削液及其制备方法
本专利技术属于机械化工领域，特别涉及一种铸铁加工过程中使用的切削液。
技术介绍
切削液是一种用在金属切削、磨加工过程中，用来冷却和润滑刀具和加工件的工业用液体，切削液由多种超强功能助剂经科学复合配合而成，同时具备良好的冷却性能、润滑性能、防锈性能、除油清洗功能、防腐功能、易稀释特点。铸铁主要由铁、碳和硅组成的合金的总称。一般而言，含碳量超过2%的合金即是我们认为的铸铁。通常情况下，在加工车间进行铸件的精加工，但是由于铸铁件的性质，加工铸件会产生烟尘，这些烟尘对于加工机床等工具会造成影响，会加速工具的磨损，降低工具的精度；而且在使用切削液的过程中，会对铸铁造成不同程度的腐蚀，因此，切削液在铸铁件加工过程中的防锈性能也极为重要。
技术实现思路
本专利技术解决的技术问题：针对上述不足，克服现有技术的缺陷，本专利技术的目的是提供一种用于铸铁加工防锈的切削液及其制备方法。本专利技术的技术方案：一种铸铁加工防锈切削液，由以下质量份数的各个组分组成：双季戊四醇酯3-8份、苯二甲酸二辛酯3-6份、油酸环氧酯2-4份、二聚酸1-2份、超细硅酸铝0.5...
【技术保护点】
1.一种铸铁加工防锈切削液，其特征在于，由以下质量份数的各个组分组成：双季戊四醇酯，3‑8份；苯二甲酸二辛酯，3‑6份；油酸环氧酯，2‑4份；二聚酸，1‑2份；超细硅酸铝，0.5‑2.5份；丙烯酸乳液，4‑10份；去离子水，55‑80份；抗氧防腐剂，0.8‑2.5份；防锈剂，1‑3份。
【技术特征摘要】
1.一种铸铁加工防锈切削液，其特征在于，由以下质量份数的各个组分组成：双季戊四醇酯，3-8份；苯二甲酸二辛酯，3-6份；油酸环氧酯，2-4份；二聚酸，1-2份；超细硅酸铝，0.5-2.5份；丙烯酸乳液，4-10份；去离子水，55-80份；抗氧防腐剂，0.8-2.5份；防锈剂，1-3份。2.根据权利要求1所述的铸铁加工防锈切削液，其特征在于：所述抗氧防腐剂为硫磷烷基酚锌盐或硫磷二烷基锌盐。3.根据权利要求1所述的铸铁加工防锈切削液，其特征在于：所述...
【专利技术属性】
技术研发人员：秦波，
申请(专利权)人：江苏宝机数控科技有限公司，
类型：发明
国别省市：江苏,32