本发明专利技术涉及一种用于胰岛素保温12~18℃相变蓄冷剂，属于生物药品保温领域。本发明专利技术以相变石蜡为原料，添加正十六烷及膨胀石墨混合均质后制得。本发明专利技术制备的相变蓄冷剂材料能够提高蓄冷速率，相变温度在12~18℃，相变潜热达260~290kJ/kg，相变潜热高，蓄冷效果好；本发明专利技术制备的相变蓄冷材料呈流动状，粘度较小，便于实现工业化生产。

A Phase Change Cooling Storage Agent for Insulin Thermal Insulation at 12-18 C

The invention relates to a phase change refrigerant used for insulin insulation at 12 - 18 C, belonging to the field of biological medicine insulation. The invention is prepared by mixing phase change paraffin as raw material, adding n-hexadecane and expanded graphite to homogenize. The phase change refrigerant material prepared by the invention can improve the refrigeration storage rate, the phase change temperature is 12-18 C, the latent heat of phase change reaches 260-290kJ/kg, the latent heat of phase change is high, and the refrigeration storage effect is good; the phase change refrigerant material prepared by the invention has the characteristics of flow, low viscosity, and is convenient for industrial production.

【技术实现步骤摘要】
一种用于胰岛素保温12~18℃相变蓄冷剂
本专利技术涉及一种用于胰岛素保温12～18℃相变蓄冷剂，属于生物药品保温领域。
技术介绍
随着人们生活水平的提高、生活节奏的加快及生活习惯的改变，糖尿病患者数呈现逐年上升的趋势，同时趋向年轻化。特别是患有型糖尿病的患者，必须依靠体外注射胰岛素进行血糖调节。胰岛素属于一种生物制剂，其贮藏和保存有着严格的环境条件，未开封的胰岛素需在2～8℃温度环境下长期保存，未开封或开封后的胰岛素可贮藏在2～25℃温度环境下短期保存。胰岛素的贮藏条件严重限制了型糖尿病的患者的出行。目前市场上出现的用于胰岛素保温的冷藏盒依靠有源制冷，且保温时间短，盒体较重，给患者带来出行不便。因此，若能够实现无源制冷、长时间保冷，对型糖尿病的患者的出行带来极大便利，用于胰岛素保温的蓄冷剂将有较为广阔的市场前景。
技术实现思路
本专利技术的目的是提供一种12～18℃的相变蓄冷剂，用于胰岛素保温的相变蓄冷剂。本专利技术是一种用于胰岛素保温12～18℃相变蓄冷剂，其特征在于：由相变石蜡、正十六烷、膨胀石墨构成，质量分数如下：相变石蜡质量分数为8%~30%，正十六烷质量分数为50%～90%，本文档来自技高网...

【技术保护点】
1.一种于胰岛素保温12~18℃相变蓄冷剂，其特征在于：由相变石蜡、正十六烷、膨胀石墨构成，质量分数如下：相变石蜡质量分数为8%~30%，正十六烷质量分数为50%～90%，膨胀石墨质量分数为5%~15%。

【技术特征摘要】
1.一种于胰岛素保温12~18℃相变蓄冷剂，其特征在于：由相变石蜡、正十六烷、膨胀石墨构成，质量分数如下：相变石蜡质量分数为8%~30%，正十六烷质量分数为50%～90%，膨胀石墨质量分数为5%~15%。2.权利要求1所述一种胰岛素保温12~18℃相变蓄冷剂，其特征在于：所述相变石蜡的相变温度为12~18℃。3.权利要求1所述一...