The invention relates to a concrete water reducing agent and a preparation method thereof, belonging to the technical field of concrete additives. The water reducing agent of the invention includes: allyl polyethanol with a molecular weight of 400, allyl polyethanol with a molecular weight of 500, allyl polyethanol with a molecular weight of 1000, maleic anhydride, sodium vinyl sulfonate, citrate methacrylate, deionized water, acrylic acid, methacrylic acid, sodium methacrylate, hydroxyethyl acrylate, ammonium persulfate and calcium bicarbonate. The invention has good dispersibility and dispersion retention, and has good early strength effect. The water reducing agent with good dispersibility and dispersion retention was prepared by free radical polymerization in aqueous solution using allyl polyethanol, maleic anhydride and sodium vinyl sulfonate with different molecular weights as polymeric monomers.
【技术实现步骤摘要】
一种混泥土减水剂及其制备方法
本专利技术涉及一种减水剂及其制备方法，更具体地说，本专利技术涉及一种混泥土减水剂及其制备方法，属于混凝土添加剂
技术介绍
减水剂是一种在维持混凝土坍落度不变的条件下，能减少拌合用水量的混凝土外加剂。大多属于阴离子表面活性剂，有木质素磺酸盐、萘磺酸盐甲醛聚合物等。加入混凝土拌合物后对水泥颗粒有分散作用，能改善其工作性，减少单位用水量，使混凝土强度增加并改善耐久性；或减少单位水泥用量，节约水泥。国家知识产权局于2006.6.28公开了一件公开号为CN1792960，名称为“一种马来酸酐系混凝土减水剂及制备方法”的专利技术专利，该专利公开了一种马来酸酐系混凝土减水剂及制备方法，由甲氧基聚乙二醇与马来酸酐反应生成马来酸单甲氧基聚乙二醇酯单体，利用合成的大单体，与2-丙烯酰胺-2甲基丙基磺酸钠共聚合成含有羧基，磺酸基和聚氧乙烯链侧链的高分子，即为马来酸酐系混凝土减水剂。本专利技术制得的马来酸酐系混凝土减水剂，碱含量低，减水率高，在以胶凝材料质量的0.6%～1.5%加入时，混凝土操作省力，水泥拌合物具有高流动性，良好的和易性，可有效抑制...
【技术保护点】
1.一种混泥土减水剂，其特征在于：包括以下按照重量份数计的原料：A组分分子量为400的烯丙基聚乙醇 10‑15份分子量为500的烯丙基聚乙醇 5‑10份分子量为1000的烯丙基聚乙醇 5‑10份马来酸酐 3‑5份乙烯基磺酸钠 3‑5份甲基丙烯酸柠檬酸酯 2‑8份去离子...
【技术特征摘要】
1.一种混泥土减水剂，其特征在于：包括以下按照重量份数计的原料：A组分分子量为400的烯丙基聚乙醇10-15份分子量为500的烯丙基聚乙醇5-10份分子量为1000的烯丙基聚乙醇5-10份马来酸酐3-5份乙烯基磺酸钠3-5份甲基丙烯酸柠檬酸酯2-8份去离子水70-130份；B组分丙烯酸3-5份甲基丙烯酸5-10份甲基丙烯基磺酸钠5-10份丙烯酸羟乙酯3-5份C组分去离子水10-20份过硫酸铵0.5-1.0份碳酸氢钙0.5-1.0份。2.根据权利要求1所述的一种混泥土减水剂的制备方法，其特征在于：包括以下工艺步骤：A、按配方要求称取烯丙基聚乙醇、马来酸酐、乙烯基磺酸钠、甲基丙烯酸柠檬酸酯和去离子水，加入带有搅拌的三口瓶中，充分搅拌均匀，得到A组分，备用；B、按配方要...