一种制备仿陶瓷花盆的方法技术

本发明专利技术公开了一种制备仿陶瓷花盆的方法，是将氧化镁、氯化镁、重钙粉、铁矿粉、色基、水按量配好后搅拌、注模成型、烘干固化、脱模、修坯、抛光得产品。按本制备方法制备的产品为免烧制品，制备工艺简单，设备投资少，能耗低，成本低，所生产的制品产品外形、强度同陶瓷紫砂制品，可用于园林绿化、盆景栽培等。

A Method of Preparing Imitated Ceramic Flower Pots

The invention discloses a method for preparing a ceramic-like flowerpot. The product is obtained by mixing magnesia, magnesium chloride, heavy calcium powder, iron ore powder, color base and water according to the amount, casting, drying and curing, demoulding, trimming and polishing. The product prepared according to the preparation method is a non-burning product. The preparation process is simple, the equipment investment is low, the energy consumption is low, and the cost is low. The product has the same shape and strength as the ceramic purple sand product, and can be used for landscape greening, bonsai cultivation, etc.

【技术实现步骤摘要】
一种制备仿陶瓷花盆的方法
本专利技术涉及一种制备仿陶瓷花盆的方法。
技术介绍
我国陶瓷制品之乡为景徳镇，其陶瓷制品享誉海内外，它大多采用陶瓷生产工艺设计制造，其能源消耗高、成本高、售价高，如运到边远地区，其路遥千里，运费也高，因而增加了园林绿化及盆栽的成本。
技术实现思路
本专利技术的目的是针对陶瓷花盆尚存在的问题，旨在提供一种生产仿陶瓷花盆的制备方法，制备方法工艺简单，设备投资少，能耗低，免烧，生产的制品外形、强度同陶瓷盆。本专利技术目的的实现方式为，仿陶瓷花盆的制备方法，按重量比％取：氧化镁40-45氯化镁20-30碳酸重钙粉4-8铁矿粉10-18色基2-5水余量混合，用搅拌机搅拌，注模成型，在干燥烘房烘干固化7-9小时后脱模，修坯、抛光得制品。本专利技术选用常用的矿物原料、化工原料为原料，色基采用可形成陶瓷色的海碧兰、赤色、墨绿色色素，原料易得。原料按比例混合在搅拌机中搅拌均匀，而后注入模中，在振动台振动塌实，使结构致密、成型，而后在干燥烘房中于70℃-90℃下烘干6-8小时后脱模、修坯，用抛光机抛光得制品。本制备方法工艺简单、设备投资少、能耗低、成本低，所生产的制品为免烧制品，外本文档来自技高网...

【技术保护点】
1.一种制备仿陶瓷花盆的方法，其特征在于按重量比％取： 氧化镁40‑45 氯化镁20‑30 碳酸重钙粉4‑8 铁矿粉10‑18 色 基2‑45 水 余量 混合，用搅拌机搅拌，注模成型，在干燥烘房于70℃‑90℃下烘干固化 6‑8小时后脱模、修坯、抛光得制品。

【技术特征摘要】
1.一种制备仿陶瓷花盆的方法，其特征在于按重量比％取：氧化镁40-45氯化镁20-30碳酸重钙粉4-8铁矿粉10-18色基2-45水余量混合，用搅拌机搅拌，...

【专利技术属性】
技术研发人员：高仁丽，
申请(专利权)人：高仁丽，
类型：发明
国别省市：江苏,32