本发明专利技术公开了一种石墨烯混凝土界面剂，其由液料和粉料组成，其中，液料由如下组分和重量份组成：丙烯酸酯水性复膜胶55‑79份，氧化石墨烯水溶液38‑46份，水8‑19份，防腐剂0.01‑0.03份，消泡剂0.01‑0.02份；粉料由如下组分和重量份组成：水洗河砂60‑76份，普通硅酸盐水泥40‑53份，消泡粉0.01‑0.03份；液料和粉料按重量配合比为1∶2.6配合使用。本发明专利技术石墨烯混凝土界面剂可用于未粉刷前的混凝土光滑面、混凝土天花板面等，本石墨烯混凝土界面剂与粉刷的水泥砂浆找平层相容性好，粘结强度高。

A Graphene Concrete Interface Agent

The invention discloses a graphene concrete interface agent, which is composed of liquid material and powder material. The liquid material is composed of the following components and weight components: acrylate water-borne laminating adhesive 55 79, graphene oxide water solution 38 46, water 8 19, preservative 0.01 0.03, defoamer 0.01 0.02; and powder is composed of the following components and weight components: water washing River sand 60 76, general Portland cement 40 53, defoaming powder 0.01 0.03; liquid and powder mix ratio 1 2.6 by weight. The graphene concrete interface agent of the invention can be used for smooth surface of concrete and concrete ceiling surface before uncoating. The graphene concrete interface agent has good compatibility with the plastering cement mortar leveling layer and high bonding strength.

【技术实现步骤摘要】
一种石墨烯混凝土界面剂
本专利技术属于建筑材料
，具体涉及一种石墨烯混凝土界面剂。
技术介绍
目前在天花板或顶部楼板使用混凝土，需使用模板支撑进行。也就是先固定好模板，然后在模板上浇筑混凝土。静置一段时间，待混凝土凝固后，进行拆模，也就是松掉模板。此时天花板上的混凝土表面大部分是平整的、光滑的，但也有高低不平的部分，为了使混凝土表面平整度达到一定的平整要求，则需要在混凝土表面上在用水泥砂浆找平。此时继续用水泥砂浆找平，则容易出现水泥砂浆找平层脱落下来，从而导致安全问题。传统的处理方法是进行凿毛处理，以增大混凝土的粘结力，但该处理方法的效果不理想，且费工费时。
技术实现思路
有鉴于此，本专利技术的目的在于提供一种石墨烯混凝土界面剂，其可用于未粉刷前的混凝土光滑面、混凝土天花板面等，该石墨烯混凝土界面剂与粉刷的水泥砂浆找平层相容性好，粘结强度高。所采用的技术方案为：一种石墨烯混凝土界面剂，其由液料和粉料组成，其中，液料由如下组分和重量份组成：粉料由如下组分和重量份组成：水洗河砂60-76份，普通硅酸盐水泥40-53份，消泡粉0.01-0.03份；液料和粉料按重量配合比为1∶2.6配合使本文档来自技高网...

【技术保护点】
1.一种石墨烯混凝土界面剂，其特征在于，其由液料和粉料组成，其中，液料由如下组分和重量份组成：

【技术特征摘要】
1.一种石墨烯混凝土界面剂，其特征在于，其由液料和粉料组成，其中，液料由如下组分和重量份组成：粉料由如下组分和重量份组成：水洗河砂60-76份，普通硅酸盐水泥40-53份，消泡粉0.01-0.03份；液料和粉料按重量配...