The invention relates to a concrete, in particular to a concrete containing coal gangue slag, belonging to the technical field of concrete. A concrete containing coal gangue slag is characterized in that the concrete containing coal gangue slag comprises the following components: 42.5 cement 400 800 parts, vitrified Beads 50 80 parts, coal gangue slag 100 200 parts, CTF concrete synergist 20 30 parts, water reducer 10 20 parts, silica fume 100 400 parts, water 100 200 parts. By adjusting the proportioning of concrete, the concrete can form an ideal permeable concrete structure, and the concrete pavement has high strength and permeability, and the compressive and flexural strength of the permeable concrete can be improved.
【技术实现步骤摘要】
一种含有煤矸石炉渣的混凝土
本专利技术涉及一种混凝土，具体涉及一种含有煤矸石炉渣的混凝土，属于混凝土
技术介绍
透水性混凝土是由骨料、水泥和水拌制而成的一种多孔轻质混凝土，它不含细骨料，由粗骨料表面包覆一薄层水泥浆相互粘结而形成孔穴均匀分布的蜂窝状结构，故具有透气、透水和重量轻的特点，作为环境负荷减少型混凝土，透水性混凝土的研究开发越来越受到重视。随着经济的发展和城市建设的加快，现代城市的地表逐步被建筑物和混凝土路面覆盖。便捷的交通设施、平整铺设的道路给人们的出行带来了极大的方便，但这些不透水的路面也给城市的生态环境带来诸多负面的影响。由于混凝土铺筑的路面缺乏透水性和透气性，雨水不能渗入地下，致使地表植物由于严重缺水而难以正常生长；不透气的路面很难与空气进行热量、水分的交换，缺乏对城市地表温度、湿度的调节能力，产生所谓的“热岛现象”。此外，不透水的道路表面容易积水，降低道路的舒适性和安全性。当短时间内集中降雨时，雨水只能通过下水设施排入河流，大大加重了排水设施的负担。公开日为2014年9月10日、公开号为CN104030640A的中国专利技术专利申请公开...
【技术保护点】
1.一种含有煤矸石炉渣的混凝土，其特征在于，所述含有煤矸石炉渣的混凝土包括以下重量份的各组分：42.5号水泥400‑800份，玻化微珠 50‑80份，煤矸石炉渣 100‑200份，CTF混凝土增效剂20‑30份，减水剂10‑20份，硅灰 100‑400份，水100‑200份。
【技术特征摘要】
1.一种含有煤矸石炉渣的混凝土，其特征在于，所述含有煤矸石炉渣的混凝土包括以下重量份的各组分：42.5号水泥400-800份，玻化微珠50-80份，煤矸石炉渣100-200份，CTF混凝土增效剂20-30份，减水剂10-20份，硅灰100-400份，水100-200份。2.根据权利要求1所述的含有煤矸石炉渣的混凝土，其特征在于，所述含有煤矸石炉渣的混凝土包括以下重量份的各组分：42.5号水泥440-760份，玻化微珠54-76份，煤矸石炉渣110-187份，CTF混凝土增效剂21.8-29.30份，减水剂11-19份，硅灰130-380份，水118-184份。3.根据权利要求1所述的含有煤矸石炉渣的混凝土，其特征在于，所述含有煤矸石炉渣的混凝土包括以下重量份的各组分：42.5号水泥460-722份，玻化微珠58-7...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。