The invention discloses a preparation method of flower-shaped cobalt hydroxide with high electrocatalytic activity, which includes the following steps: step 1, dissolve 1 mmol-1 mol CoSO4.7H_2O as Co source in deionized water, and obtain solution A after complete dissolution; step 2, add 0.5 mmmol-2 mol hydrazine hydrate N2H_4.H_2O to solution A obtained in step 1, stir for 1-10 h at room temperature, and centrifuge statically. Deionized water is washed 3 to 6 times by centrifugation and dried. The invention overcomes the technological requirements of the traditional preparation method requiring high temperature, heating or template, greatly reduces the preparation cost and equipment requirements, and is easy to achieve mass production.
【技术实现步骤摘要】
一种高电催化活性三维曲面花状氢氧化钴的制备方法
本专利技术属于氢氧化钴的制备
，具体涉及一种高电催化活性三维曲面花状氢氧化钴的制备方法。
技术介绍
氢能被认为是21世纪最有前景的清洁能源之一，电解水制氢因其工艺简单，得到的氢气纯度高，受到了广泛的关注。然而，电解水制氢包括析氢反应与析氧反应两个半反应，其中析氧反应涉及到四电子转移过程，所以严重的影响到了整个反应的整体反应速率，而且，在诸多能量转换器，比如：金属-空气电池，可再生燃料电池中，均会涉及到析氧反应。因此开发制备无毒、低成本、高活性的析氧反应电催化剂对清洁能源及能量转换器的发展都具有非常重要的意义。Co基材料很早以前就被认为是理想的电解水催化材料，因为其价格低廉并且储量丰富，在大规模应用方面的潜力明显优于IrO2、RuO2等贵金属氧化物电催化剂，并且在碱性电解液中具有优异的电催化性能。氧化钴，硫化钴，氢氧化钴及磷化钴等Co基材料已被广泛的应用于电催化水氧化。通常来讲，Co基催化剂的制备包含两个步骤，首先合成Co离子前驱体，然后进行水热、高温或磷化等处理过程来获得产品。反应过程复杂并且耗能较大，有的反应...
【技术保护点】
1.一种高电催化活性三维曲面花状氢氧化钴的制备方法，其特征在于：具体包括如下步骤：步骤1，将1mmol～1mol CoSO4·7H2O作为Co源溶于去离子水中，完全溶解后，得溶液A；步骤2，向步骤1所得的溶液A中加入0.5mmol～2mol水合肼N2H4·H2O，在室温下搅拌1～10h，静置离心，用去离子水离心洗涤3～6次，干燥，即得。
【技术特征摘要】
1.一种高电催化活性三维曲面花状氢氧化钴的制备方法，其特征在于：具体包括如下步骤：步骤1，将1mmol～1molCoSO4·7H2O作为Co源溶于去离子水中，完全溶解后，得溶液A；步骤2，向步骤1所得的溶液A中加入0.5mmol～2mol水合肼N2H4·H2O，在室温下搅拌1～10h，静置离心，用去离子...
【专利技术属性】
技术研发人员：王媛，严珂，李智敏，黄云霞，闫养希，
申请(专利权)人：西安电子科技大学，
类型：发明
国别省市：陕西,61
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。