一种使用凹凸棒石黏土修复尾矿中重金属的方法技术

本发明专利技术属于环境保护技术领域，具体涉及一种使用凹凸棒石黏土修复矿尾中重金属的方法。本发明专利技术是向尾矿中添加凹凸棒石黏土，充分搅拌均匀，所述的凹凸棒石黏土的添加量占尾矿重量5％～15％，直到尾矿中重金属含量与尾矿所在地土壤的重金属背景值一致。本方法主要是对尾矿中的重金属进行原位修复，该方法相比中和法、电化学法、隔离法、生物处理法等，具有操作简单，容易施工，成本低的优点，可在大面积的尾矿修复应用。

A method of repairing heavy metals in tailings with attapulgite clay

The invention belongs to the technical field of environmental protection, in particular to a method for repairing heavy metals in tailings by using attapulgite clay. The invention adds attapulgite clay to tailings and mixes well. The additive amount of the attapulgite clay accounts for 5%-15% of the tailings weight until the content of heavy metals in the tailings is consistent with the background value of heavy metals in the soil where the tailings are located. Compared with neutralization method, electrochemical method, isolation method and biological treatment method, this method has the advantages of simple operation, easy construction and low cost, and can be applied in large-scale tailings restoration.

【技术实现步骤摘要】
一种使用凹凸棒石黏土修复尾矿中重金属的方法
本专利技术属于环境保护
，具体涉及一种使用凹凸棒石黏土修复矿尾中重金属的方法。
技术介绍
尾矿是矿山选矿的副产物，是一种没有强度、含有污染物、极易液化流动的高含水率固体废物。我国是一个金属矿山资源极其丰富的大国，且对矿山的开发利用强度大，每年会产生数量巨大的尾矿，据统计，我国现存尾矿量超过百亿吨，且每年以数亿吨的速度增长，但尾矿的综合利用率很低，绝大多数尾矿尚未被综合利用而是选择堆存，大量的堆存的尾矿不仅占用土地、造成资源浪费，还会带来严重的环境污染。尾矿粒径较小，比表面积大，尾矿本身也是一个典型的污染点源，尾矿中有害成分尤其是重金属随着地表水和地下水进入水环境或直接进入土壤，直接或间接地造成土壤和水环境重金属污染，严重胁迫人类健康。目前，国内外在修复尾矿重金属中已有表面钝化法相关报道，表面钝化法是利用化学反应在尾矿颗粒表面形成一层不溶的、惰性的和致密的膜，从而使氧气和其它氧化剂无法侵袭尾矿。该法是从微观单个颗粒水平来保护尾矿。目前研究比较多的表面钝化法有：磷酸盐钝化法、硅酸盐钝化法和有机盐钝化法等。但是目前国内外发现的有效的表面钝化本文档来自技高网...

【技术保护点】
1.一种使用凹凸棒石黏土修复尾矿中重金属的方法，其特征在于按照以下步骤进行：向尾矿中添加凹凸棒石黏土，充分搅拌均匀，所述的凹凸棒石黏土的添加量占尾矿重量5％～15％，直到尾矿中重金属含量与尾矿所在地土壤的重金属背景值一致。

【技术特征摘要】
1.一种使用凹凸棒石黏土修复尾矿中重金属的方法，其特征在于按照以下步骤进行：向尾矿中添加凹凸棒石黏土，充分搅拌均匀，所述的凹凸棒石黏土的添加量占尾矿重量5％～15％，直到尾矿中重金属含量与尾矿所在地土壤的重金属背景值一致。...

【专利技术属性】
技术研发人员：邓鹏宏，许灏，高江，赵虹，魏宏贺，王海龙，
申请(专利权)人：鞍钢集团矿业有限公司，
类型：发明
国别省市：辽宁,21