The invention discloses a composite metal organic framework (CMOF) and a composite metal oxide organic framework (CMOOF) material and its preparation method and application in supercapacitors; the CMOF has an octahedron frame structure in micro-nano size, and the CMOOF material has a porous hollow octahedron frame structure in micro-nano size; the preparation methods of the CMOF and CMOOF material include: 1) the manufacture of CMOF; Preparation; 2) post-treatment of CMOF; 3) preparation of CMOOF; preparation methods of supercapacitors based on this material include: 1) preparation of electrode active materials; 2) cleaning of collecting fluid; 3) smear and pressing. Based on this material, the maximum specific capacitance of supercapacitors can reach 948F.g.
【技术实现步骤摘要】
复合金属-有机框架材料、复合金属氧化物-有机框架材料及制备方法与应用
本专利技术涉及一种复合金属-有机框架材料CMOF和复合金属氧化物-有机框架材料CMOOF及其制备方法与应用，属于电子材料器件领域。
技术介绍
金属-有机框架(MOF)作为一类新型的多孔材料，由有机桥联配体与过渡金属离子通过自组装形成，且具有周期性网络结构。由于比表面积高、活性金属位点开放、孔道调控灵活等特性，MOF在材料、器件与应用等多个角度已引起了广泛关注，如应用于催化、气体储存和分离、传感器、超级电容器等领域。在超级电容器中，MOF可作为合成多孔过渡金属氧化物的优异前体，此外，MOF本身可以直接用作超级电容器的电极材料，因为它们的孔隙率和金属阳离子分别提供电解质和氧化还原活性位点的容纳空间。由于MOF可控的微孔尺寸和高比表面积，其在超级电容器中具有广泛的应用前景。现有文献中，Rahmanifar等人[ElectrochimicaActa275(2018):76-86，后续记为文献1]合成一种CMOF(具体为Ni-Co-MOF)，其形貌为球型，文章先后合成Ni-MOF和Co-MOF，再将两种M...
【技术保护点】
1.一种复合金属‑有机框架材料，其为微纳尺寸下的十八面体框架结构。
【技术特征摘要】
1.一种复合金属-有机框架材料，其为微纳尺寸下的十八面体框架结构。2.权利要求1所述复合金属-有机框架材料的制备方法，其特征在于，包括下述步骤：1)CMOF的制备：先配制二甲基咪唑水溶液，再配制CTAB水溶液，然后将Co(NO3)2·6H2O、MnCl2·4H2O依次加入CTAB水溶液中，最后将二甲基咪唑水溶液加入CTAB水溶液中，混合搅拌，然后静置，得到含CMOF沉淀的悬浮液；2)CMOF的后处理：将步骤1)中所得的悬浮液用高速离心机离心洗涤并用真空干燥箱干燥，得到CMOF粉末，即为复合金属-有机框架材料。3.如权利要求2所述复合金属-有机框架材料的制备方法，其特征在于，所述步骤1)中，CTAB、二甲基咪唑、Co(NO3)2·6H2O和MnCl2·4H2O的质量比为1：(908～1135)：(58～73)：(78～98)。4.如权利要求2所述复合金属-有机框架材料的制备方法，其特征在于，所述步骤1)中，混合溶液搅拌时间为10～30min，静置时间为3～4h；所述步骤2)中，离心速度为7000～9000rad/min，离心时间为8～12min；洗涤次数为5-10次；干燥温度为60～80℃，干燥时间为8～12h。5.一种复合金属氧化物-有机框架材料，其特征在于，将权利要求2-4任一项所述制备方法...
【专利技术属性】
技术研发人员：曾玮，周小雯，卫宁，王强，马悦，梁栋，徐超，黄林生，
申请(专利权)人：安徽大学，
类型：发明
国别省市：安徽,34