A preparation method of molybdenum disulfide bio-functional coating based on magnetron sputtering on titanium sheet surface includes the following steps: S1, alkali heat treatment on titanium sheet surface; S2, sputtering molybdenum disulfide coating on titanium sheet surface through magnetron sputtering system. The advantages are: uniform molybdenum disulfide layer can be formed on the surface of titanium sheet by using magnetron sputtering system; moreover, the working pressure, deposition time and deposition rate of the magnetic control system can effectively control the morphology and thickness of molybdenum disulfide layer; the device of the invention has less investment, less implementation difficulty, simple preparation method, and has little impact on the environment.
【技术实现步骤摘要】
一种基于钛片表面磁控溅射二硫化钼生物功能涂层的制备方法
本专利技术涉及生物医用材料
，具体地说是一种基于钛片表面磁控溅射二硫化钼生物功能涂层的制备方法。
技术介绍
生物医用材料是一类新型材料，也是一种特殊的功能材料，是用来对生物体进行诊断、治疗、修复或替换其病损组织、器官或增进其功能，且对生物体组织不会产生不良影响的材料。生物医用材料根据其组成和结构可以分为以下五大类：金属材料、高分子材料、医用复合材料、无机非金属材料或生物陶瓷、生物衍生材料。由于生物医用金属材料具有优良的力学性能，易加工性和热稳定性，因此被广泛应用于牙科，整形外科等领域。其中医用钛金属材料是目前骨科常用的内固定材料，作为植入物材料在骨科内固定手术中，尤其在负载部位得到了广泛的应用。在外科手术进行之前，通常都会对所用的手术专用医疗器械及植入器件进行一系列非常严格的灭菌消毒过程，但是这些措施并不能完全保证病人不会受到细菌的感染，而且对器材消毒灭菌的作用时间短、成本高。而一旦发生感染，不能及时根除，细菌形成生物保护膜，则需要长期依赖抗生素甚至多次手术才能治愈，这种情况在造成各种经济损失的同时还给...
【技术保护点】
1.一种基于钛片表面磁控溅射二硫化钼生物功能涂层的制备方法，其特征在于：包括如下步骤S1、对钛片表面进行碱热处理；S2、通过磁控溅射系统在钛片表面溅射二硫化钼涂层。
【技术特征摘要】
1.一种基于钛片表面磁控溅射二硫化钼生物功能涂层的制备方法，其特征在于：包括如下步骤S1、对钛片表面进行碱热处理；S2、通过磁控溅射系统在钛片表面溅射二硫化钼涂层。2.根据权利要求1所述方法，其特征在于：步骤S1中，碱热处理具体是：将钛片放入盛有浓度为3-5mol/L的KOH溶液的反应釜中，再将反应釜放入烘箱中于70-90℃条件下反应90-120min后，取出洗涤干燥。3.根据权利要求1所述方法，其特征在于：碱热处理之前，需先将钛片打磨后依次在丙酮、蒸...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。