The invention discloses a hot working die steel and a preparation method thereof. Steel contains C:0.45%-0.55%, Cr:5.50%-6.50%, Si:0.85%-1.10%, Mn:0.30%-0.50%, Mo:1.20%-1.50%, V:0.60%-1.00%, P<0.013%, S<0.03%, Gd:0.15%-0.25%, La:0.10%-0.15%, Y:0.10%-0.15%, the rest are Fe and inevitable impurities. In electric furnace smelting, billet heating temperature is 1200-1280 C, holding time is 2-4 h, start rolling temperature is 1150-1250 C, finish rolling temperature is 820-950 C, cooling speed is 5-10 C/s, and final cooling temperature is 400-550 C. The first stage is isothermal annealing temperature 830-880 C, the second stage is isothermal annealing temperature 730-780 C, quenching temperature 1050-1150 C, tempering temperature 550-650 C. The hot work die steel produced has high orientation and impact resistance.
【技术实现步骤摘要】
一种热作模具钢及其制备方法
本专利技术属于高合金钢生产领域，特别涉及一种具有高等向性及抗冲击性的热作模具钢材料。
技术介绍
如今，我国的模具行业迅速发展，在世界范围内中国模具制造比例逐步提高，模具钢的用量也在显著增加。热作模具钢作为模具钢中的重要组成部分，近年来取得较大进展，但其服役条件十分恶劣，合金元素含量较高，组织结构较为复杂，所以对其性能的要求更加苛刻。目前，常规模具钢应用中存在性能单一，使用寿命较短等问题，为了提高热作模具钢的综合性能，可采用添加稀土元素来改善析出相的组成、分布、形貌，改变碳化物及夹杂物形态、细化晶粒、净化和强化晶界等来提高其性能。针对热作模具中添加稀土元素来提高性能，国内外研究学者进行大量研发工作并取得一定成果。邓开国，李长荣，杨远梅在《中国稀土学报》，2016年，第34卷第4期中发表的论文《铈元素对H13模具钢等向性能的研究》中提出了在H13模具钢中添加Ce元素含量0.05％时，H13的等向性能大幅度提高，横纵向力学性能均呈上升趋势，但其硬度显著降低。陈研在《铸造技术》，2014年，第35卷第4期中发表的论文《稀土元素Gd和Sc对H13...
【技术保护点】
1.一种热作模具钢，其特征在于，钢中化学成分按质量百分比为：C：0.45％～0.55％，Cr：5.50％～6.50％，Si：0.85％～1.10％，Mn：0.30％～0.50％，Mo：1.20％～1.50％，V：0.60％～1.00％，P≤0.013％，S≤0.03％，Gd：0.15％～0.25％，La：0.10％～0.15％，Y：0.10％～0.15％，其余为Fe和不可避免的杂质。
【技术特征摘要】
1.一种热作模具钢，其特征在于，钢中化学成分按质量百分比为：C：0.45％～0.55％，Cr：5.50％～6.50％，Si：0.85％～1.10％，Mn：0.30％～0.50％，Mo：1.20％～1.50％，V：0.60％～1.00％，P≤0.013％，S≤0.03％，Gd：0.15％～0.25％，La：0.10％～0.15％，Y：0.10％～0.15％，其余为Fe和不可避免的杂质。2.一种如权利要求1所述的热作模具钢的制备方法，钢板的生产工艺为：包括铁水预处理，电炉冶炼、铸造、热轧、热处理，其特征在于，热轧工艺中，钢坯的加热温度为12...
【专利技术属性】
技术研发人员：冯丹竹，赵坦，范刘群，李云，石峰涛，刘浩岩，
申请(专利权)人：鞍钢股份有限公司，
类型：发明
国别省市：辽宁,21