The invention discloses a ceramic glaze and a porcelain made from the ceramic glaze. The ceramic glaze comprises the following raw materials of mass percentage: glass powder 31%-43%, zinc oxide 16%-26%, quartz 10%-18%, titanium dioxide 7%-14%, talcum powder 3%-6%, melt 0.2%-0.5%, copper oxide 1.5%-3%, iron oxide 0.6%-1.5%, manganese oxide 2.5-4%, armor. Base cellulose is 0.02%-0.04%, potassium feldspar is 2%-4%, glaze mud is 5%-7%, glaze mud is black mud or bentonite, or mixture of black mud and bentonite. The enamel fired by the formula of the invention has smooth and smooth glaze surface, natural and beautiful surface texture. The glaze surface is observed under a 200-fold microscope. The crystal flowers on the glaze surface are intact, and there are almost no micro-cracks. The Mohs hardness is 5_7, and the fracture modulus can reach 85.3 MPa. The glaze surface is not easy to crack. It has long service life and high economic value.
【技术实现步骤摘要】
陶瓷釉料及瓷器
本专利技术涉及陶瓷
，具体涉及一种陶瓷釉料及使用该陶瓷釉料制成的瓷器。
技术介绍
陶瓷材料作为无机非金属材料的一个重要门类，取得了很大的发展。结构陶瓷以其高机械强度、高硬度、耐腐蚀性等优点被广泛用于冶金、矿厂及航天等领域。目前市面上出现的陶瓷产品中，很多都存在釉面容易开裂的问题，其主要原因是釉面不够光滑，断裂模数较低，虽然各产品从宏观表面看很完美，但在显微镜下观察会发现有较多细小的微裂纹和凹坑，由于这些微裂纹和凹坑在瓷器的使用过程中会逐渐发展为更大的裂纹，导致这些瓷器的使用寿命较短、经济价值较低。
技术实现思路
有鉴于此，本专利技术有必要提供一种可制备表面光滑、微裂纹较少、釉面不易开裂的瓷器的陶瓷釉料。具体技术方案如下：一种陶瓷釉料，包括以下质量百分比的原料：玻璃粉31％～43％、氧化锌16％～26％、石英10％～18％、钛白粉7％～14％、滑石粉3％～6％、熔块0.2％～0.5％、氧化铜1.5％～3％、氧化铁0.6％～1.5％、氧化锰2.5～4％、甲基纤维素0.02％～0.04％、钾长石2％～4％、釉用泥5％～7％，所述的釉用泥为黑泥或膨润土，...
【技术保护点】
1.一种陶瓷釉料，其特征在于，包括以下质量百分比的原料：玻璃粉31％～43％、氧化锌16％～26％、石英10％～18％、钛白粉7％～14％、滑石粉3％～6％、熔块0.2％～0.5％、氧化铜1.5％～3％、氧化铁0.6％～1.5％、氧化锰2.5～4％、甲基纤维素0.02％～0.04％、钾长石2％～4％、釉用泥5％～7％，所述的釉用泥为黑泥或膨润土，或黑泥与膨润土的混合物。
【技术特征摘要】
1.一种陶瓷釉料，其特征在于，包括以下质量百分比的原料：玻璃粉31％～43％、氧化锌16％～26％、石英10％～18％、钛白粉7％～14％、滑石粉3％～6％、熔块0.2％～0.5％、氧化铜1.5％～3％、氧化铁0.6％～1.5％、氧化锰2.5～4％、甲基纤维素0.02％～0.04％、钾长石2％～4％、釉用泥5％～7％，所述的釉用泥为黑泥或膨润土，或黑泥与膨润土的混合物。2.根据权利要求1所述的陶瓷釉料，其特征在于，还包括以...