The invention discloses an insertion type tube sheet surfacing method, in which the tube is inserted into the break of the plate to form a circumferential surfacing weld, which comprises the following steps: step 1: cleaning the circumferential surfacing weld before welding; step 2: sequentially bottom, fill and cover welding the circumferential surfacing weld; at least one mistake is adopted in the bottom, fill and cover welding. Avoiding arcing. The staggered avoidance arc starting method, staggered layer indirect head, and grinding and cleaning of interlayer and arc starting and closing positions can achieve full penetration between layers, which can effectively improve penetration depth, high qualified rate of post-weld flaw detection, reduce a large number of rework and repair, and remarkably improve operation efficiency and quality.
【技术实现步骤摘要】
一种插入式管板堆焊方法
本专利技术属于焊接
，具体地说，涉及一种插入式管板堆焊方法。
技术介绍
现有技术中，动车组焊接构架侧梁与横梁连接处环形焊缝是一个典型的插入式管板圆周堆焊焊缝，焊缝质量等级要求高，工件结构比较复杂，与其它焊缝相比操作难度较大。由于空间限制整个圆周焊接不能一次性焊接完成，会出现多个焊接接头，接头过多会由于起、收弧缺陷而产生的层间咬边、气孔、夹杂等缺陷，随着堆焊层数增加，层间缺陷无法有效熔化并上浮，导致缺陷留存于堆焊焊层内部，影响内部质量。申请号为CN200610024859.1的中国专利公开了一种插入式小接管马鞍形埋弧自动焊，其方法为：在壳体的焊接孔上加工一圈斜坡口，将接管插入壳体的斜坡口中，用衬垫焊接于壳体内壁和接管，采用电红外线火焰预加热，采用埋弧焊机从壳体内壁一圈一圈往外焊。该方案会出现多个焊接接头，随着堆焊层数增加，层间缺陷无法有效熔化并上浮，导致缺陷留存于堆焊焊层内部，影响内部质量。有鉴于此特提出本专利技术。
技术实现思路
本专利技术要解决的技术问题在于克服现有技术的不足，提供一种插入式管板堆焊方法，该方法采用错避式起弧法，错开层间...
【技术保护点】
1.一种插入式管板堆焊方法，管插入板的破口中，形成圆周堆焊焊缝，其特征在于：包括如下步骤：步骤1：焊前清理圆周堆焊焊缝；步骤2：依次打底、填充和盖面焊接圆周堆焊焊缝；所述打底、填充和盖面焊接中至少一个采用错避式起弧法。
【技术特征摘要】
1.一种插入式管板堆焊方法，管插入板的破口中，形成圆周堆焊焊缝，其特征在于：包括如下步骤：步骤1：焊前清理圆周堆焊焊缝；步骤2：依次打底、填充和盖面焊接圆周堆焊焊缝；所述打底、填充和盖面焊接中至少一个采用错避式起弧法。2.根据权利要求1所述的插入式管板堆焊方法，其特征在于：所述错避式起弧法包括多层多道焊起弧点交错避开；每层的起弧点与上一层的起弧点错开。3.根据权利要求2所述的插入式管板堆焊方法，其特征在于：所述每层的起弧点与上一层的起弧点错开距离20-30mm。4.根据权利要求2所述的插入式管板堆焊方法，其特征在于：起弧点进行打磨处理，起弧点打磨成斜坡状。5.根据权利要求1所述的插入式管板堆焊方法，其特征在于：填充焊接采用扁平式多道焊填充法焊接。6.根据权利要求5所述的...
【专利技术属性】
技术研发人员：王宝昌，吕光宙，赵永州，王明，李延清，
申请(专利权)人：中车青岛四方机车车辆股份有限公司，
类型：发明
国别省市：山东,37