The production technology and products of light floor slab with hollow concrete balls as functional materials are characterized by the following technological steps: (1) preparation of hollow concrete balls: binary grafting of AM and AMPS superabsorbent resin spheres with a certain diameter of absorbent starch composite clay as sphere nuclei, and cement with concrete accelerator. Hollow concrete balls are prepared in disc pelletizer with fine sand mixture as binder; (2) Portland cement, sand aggregate, absorbed hollow concrete balls and water are mixed in regular proportion, and then filled into the reinforced bar mold frame to maintain to full strength.
【技术实现步骤摘要】
以空心混凝土球为功能性材料轻质楼板生产工艺及产品
本专利技术涉及建筑
,具体地说是轻质楼板生产工艺及产品。
技术介绍
由于高吸水聚合物具有无毒、对人体无刺激性、无副反应等特点,近年已经将高吸水聚合物应用于建筑行业,主要是用于混凝土的自养护。但是由于普通高吸水聚合物的缺陷,使得普通高吸水聚合物在建筑行业的使用受到很大的限制。原因是普通高吸水聚合物当水中含有少量盐、碱、酸类时,反渗透压降低,同时由于反离子的屏蔽作用,使高分子链收缩,导致树脂的吸水能力大大下降。例如,普通高吸水树脂在混凝土溶液中的吸水能力只有在去离子水中的1/10左右。将此种吸水后的普通高吸水聚合物加进混凝土拌料中会立即失水,难以在混凝土中发挥作用;同时应用手段单一,因此限制了其在建筑
应用。找到适合的耐盐碱高吸水聚合物,并改进其在建筑
的应用模式,有重大科技进步意义。
技术实现思路
本专利技术的目的是提供一种以空心混凝土球为功能性材料轻质楼板生产工艺及产品。在其生产过程中创新了高吸水聚合物的应用模式。所采取的技术方案是:以空心混凝土球为功能性材料轻质楼板生产工艺及产品,其技术特征是包括如下工艺环节:(1)空心混凝土球的制备:以有一定直径的吸水后的淀粉复合黏土二元接枝AM和AMPS高吸水树脂球状体为球核,以掺有混凝土速凝剂的水泥和细沙混合料为粘料,在盘式成球机中制备成空心混凝土球备用;(2)硅酸盐水泥、砂石骨料、吸水后的所述空心混凝土球、水按常规比例搅拌混合后,填入布好钢筋的模具框中养护至达到完全强度。以空心混凝土球为功能性材料轻质楼板,采用上述生产工艺方法制造。本专利技术提供的技 ...
【技术保护点】
1.以空心混凝土球为功能性材料轻质楼板生产工艺及产品,其技术特征是包括如下工艺步骤:(1)空心混凝土球的制备:以有一定直径的吸水后的淀粉复合黏土二元接枝AM和AMPS高吸水树脂球状体为球核,以掺有混凝土速凝剂的水泥和细沙混合料为粘料,在盘式成球机中制备成空心混凝土球备用;(2)硅酸盐水泥、砂石骨料、吸水后的所述空心混凝土球、水按常规比例搅拌混合后,填入布好钢筋的模具框中养护至达到完全强度。
【技术特征摘要】
2018.03.26 CN 20181025315541.以空心混凝土球为功能性材料轻质楼板生产工艺及产品,其技术特征是包括如下工艺步骤:(1)空心混凝土球的制备:以有一定直径的吸水后的淀粉复合黏土二元接枝AM和AMPS高吸水树脂球状...
【专利技术属性】
技术研发人员:不公告发明人,
申请(专利权)人:武夷山德邦环保节能设备制造有限公司,
类型:发明
国别省市:福建,35