The invention discloses a halogen-free acid-free flux, which comprises the following weight components: trimethyl borate 50 60 phr, methanol 30 40 phr, water 10 20 phr, sodium tetraborate 1 5 phr, boric acid 1 3 phr. In the halogen-free pickling flux, trimethyl borate is added to protect the workpiece from oxidation, trimethyl borate is hydrolyzed to form boric acid by adding water, and boric acid and sodium tetraborate are formed to form a traditional eutectic compound combination of flux, which further reduces the melting point and improves the flux by adding sodium tetraborate. Activity. Especially the addition of halogen is isolated, so that the surface of the brazed workpiece will not oxidize and blacken, and it is not easy to produce corrosion and penetrating pore, and the brazing activity is high, which makes the brazing efficiency higher.
【技术实现步骤摘要】
一种不含卤素的免酸洗助熔剂及其制作方法
本专利技术涉及钎焊
,特别涉及一种不含卤素的免酸洗助熔剂及其制作方法。
技术介绍
金属焊接分为融焊和钎焊。熔焊时被焊材料包括焊丝经融解-凝固使两种材料融为一体,常见的电焊、气焊、氩弧焊都属熔焊;钎焊时被焊接金属并不融化,而是焊接材料(焊丝)融化,并紧密贴附在被焊接材料上,利用两种材料原子之间的作用力连接在一起,常见的锡焊、铜焊、搪铅都属钎焊。传统方式上钎焊黄铜、紫铜等工件通常使用银焊膏,银焊膏通常含有卤素(氟化物或氯化物),焊后表面氧化发黑严重,需要酸洗后才能达到表面光亮。现有市面上也有一种免酸洗助熔剂开始使用配合含磷钎料,但该类免酸洗助熔剂残留工件表面,容易造成腐蚀,贯穿性气孔等问题。
技术实现思路
本专利技术的目的是提供一种表面不发黑且不易造成腐蚀及贯穿性气孔问题的不含卤素的免酸洗助熔剂及其制作方法。本专利技术的上述技术目的是通过以下技术方案得以实现的:一种不含卤素的免酸洗助熔剂,包含以下重量份的成分:硼酸三甲酯50-60份,甲醇30-40份,水10-20份,四硼酸钠1-5份,硼酸1-3份。进一步设置为,所述助熔剂中还包含四硼酸钾1-5份。进一步设置为,所述助熔剂的固含量在7-7.5份。一种不含卤素的免酸洗助熔剂的制作方法,包括如下步骤,将硼酸三甲酯和甲醇放入容器中进行搅拌,再依次将蒸馏水、四硼酸钠、硼酸、四硼酸钾加入容器中开始加热,加热时间为25-35分钟,加热温度为60-75摄氏度,加热同时进行持续回流和持续搅拌。综上所述,本专利技术具有以下有益效果:本专利技术的不含卤素的免酸洗助熔剂中,硼酸三甲酯的加入保 ...
【技术保护点】
1.一种不含卤素的免酸洗助熔剂,其特征在于:包含以下重量份数的成分,硼酸三甲酯50‑60份,甲醇30‑40份,水10‑20份,四硼酸钠1‑5份,硼酸1‑3份。
【技术特征摘要】
1.一种不含卤素的免酸洗助熔剂,其特征在于:包含以下重量份数的成分,硼酸三甲酯50-60份,甲醇30-40份,水10-20份,四硼酸钠1-5份,硼酸1-3份。2.根据权利要求1所述的一种不含卤素的免酸洗助熔剂,其特征在于:所述助熔剂中还包含四硼酸钾1-5份。3.根据权利要求1所述的一种不含卤素的免酸洗助熔剂,其特征在...
【专利技术属性】
技术研发人员:金海斌,钱似舰,王永洁,王水庆,
申请(专利权)人:浙江新锐焊接科技股份有限公司,
类型:发明
国别省市:浙江,33