一种自行车胎的制备方法技术

本发明专利技术公开了一种自行车胎的制备方法，其特征在于：以橡胶弹性体为基体配制自行车胎填充材料，自行车胎骨架材料由磁力定形和定位在模具中，将橡胶弹性体加热填充到自行车胎模具中，成型得到自行车胎。本发明专利技术的方法工艺简单，磁定位技术简化了自行车胎制备工艺，可操作性强，易于工业化，赋予自行车更多功能，适用于自行车胎领域生产推广。

A preparation method of bicycle tire

The invention discloses a bicycle tire preparation method, which is characterized in that the bicycle tire filling material is prepared with rubber elastomer as the matrix, the bicycle tire skeleton material is fixed and positioned in the mould by magnetic force, the rubber elastomer is heated and filled into the bicycle tire mould, and the bicycle tire is formed. The method of the invention has the advantages of simple process, simplified preparation process of bicycle tire by magnetic positioning technology, strong operability, easy industrialization, more functions for bicycle, and is suitable for production and popularization in the field of bicycle tire.

【技术实现步骤摘要】
一种自行车胎的制备方法
本专利技术涉及一种自行车胎的制备方法，主要应用于制备自行车胎，适用于所有种类自行车胎的制备。
技术介绍
随着共享单车的兴起，自行车胎的研究又成了热门的研究领域，自行车胎的加工虽然没有汽车自行车胎加工过程那么复杂，但也相对繁琐，国内传统的自行车胎生产工艺由四大工序组成：①塑/混炼；②压延和压出；③成型；④硫化。现有的自行车胎厂，除部分通过购入成品混炼胶而省缺第一道工序外，大多数是上述四道工序全部齐备。技术发展的不断革新，自行车胎也得到了不同程度的发展。目前，较为先进的自行车胎制备技术如：米其林推出的C3M技术。但也经历了以下五个步骤制备一条自行车胎：①连续低温混炼；②直接压出橡胶件；③成型鼓上编织/缠绕骨架层；④预硫化环状胎面；⑤自行车胎电热硫化。C3M技术关键设备是特种编织机和挤出机。C3M技术通过以成型鼓为核心，合理配置特种编织机组和挤出机组而得以实现。特种编织机环绕成型鼓编织无接头环形胎体帘布层和带束层，并环绕成型鼓缠绕钢丝得到钢丝圈。挤出机组连续低温(90℃以下)混炼胶料，压出胎侧、三角胶条以及其他橡胶件。倍耐力公司推出的MIRS技术发展到只有三步：①预本文档来自技高网...

【技术保护点】
1.一种自行车胎的制备方法，其特征在于：以弹性体为基体配制自行车胎填充材料，自行车胎骨架材料由磁力定形和定位在模具中，将弹性体加热填充到自行车胎模具中，成型得到自行车胎。

【技术特征摘要】
1.一种自行车胎的制备方法，其特征在于：以弹性体为基体配制自行车胎填充材料，自行车胎骨架材料由磁力定形和定位在模具中，将弹性体加热填充到自行车胎模具中，成型得到自行车胎。2.根据权利要求1所述的自行车胎的制备方法，其特征在于自行车胎骨架材料为一体结构，骨架材料中有磁性物质，与磁性元件作用，形成骨架材料内部张力，再依托骨架内部边界条件和模腔边界条件实现定位，完成骨架材料在模腔与自行车胎成品中的定形和定位。3.根据权利要求1所述的自行车胎的制备方法，其特征在于：其成型方式有注压成型、浇注成型或注射成型。4.根据权利要求1所述...