The invention discloses an environment-friendly plastic-wood composite board and its preparation method, which comprises: 1) chopping sesame rod and sorghum rod, soaking and beating in alkali solution, then filtering and cleaning to extract filter residue; 2) dividing polyvinyl chloride, polyvinyl alcohol, talcum powder, diisodecanol phthalate, lignin and vaseline. Mixing with filter residue to produce plastic wood material; 3) mixing and extruding the plastic wood material to produce the environmental protection plastic wood composite board. The environmental protection plastic-wood composite board has excellent environmental protection characteristics, and the preparation method has the advantages of simple process and easy access to raw materials.
【技术实现步骤摘要】
环保型塑木复合板及其制备方法
本专利技术涉及塑木材料,具体地,涉及一种环保型塑木复合板及其制备方法。
技术介绍
塑木材料,也叫木塑复合材料,顾名思义可理解为主要以塑料(聚丙烯、聚乙烯、聚氯乙烯等回收的废旧塑料)为原料,通过添加木粉、稻壳、秸秆等废植物纤维混合成新的木质材料,再经挤压、模压、注射成型等塑料加工工艺,生产出的板材或型材;其主要用于建材、家具、物流包装等行业。由于塑木材料兼备木材与塑料的双重特性,塑木材料与木质材料相比具有以下优势:吸水率低,不易变形开裂、防虫蛀、防霉变、机械性能高、防潮、耐酸碱、耐腐蚀、便于清洗。基于上述的这些特性使得塑木材料可在很多领域替代原木、塑料和铝合金,使得其是未来替代传统木材的新一代节能环保新产品,具有广泛的市场应用前景。虽然塑木材料具有上述诸多优点,但是塑木材料在生产过程中往往添加大量的助剂,进而导致塑木材料中含有大量的对环境和人体不利的化合物,如甲醛。
技术实现思路
本专利技术的目的是提供一种环保型塑木复合板及其制备方法,该环保型塑木复合板具有优异的环保特性,同时该制备方法具有工序简单和原料易得的优点。为了实现上述目的,本专利 ...
【技术保护点】
1.一种环保型塑木复合板的制备方法,其特征在于,包括:1)将芝麻杆、高粱杆切碎,接着置于碱液中浸泡且捶打,然后过滤、清洗取滤渣;2)将聚氯乙烯、聚乙烯醇、滑石粉、邻苯二甲酸二异癸酯、木质素、凡士林和所述滤渣进行混合以制得塑木材料;3)将所述塑木材料混炼、挤出成型以制得所述环保型塑木复合板。
【技术特征摘要】
1.一种环保型塑木复合板的制备方法,其特征在于,包括:1)将芝麻杆、高粱杆切碎,接着置于碱液中浸泡且捶打,然后过滤、清洗取滤渣;2)将聚氯乙烯、聚乙烯醇、滑石粉、邻苯二甲酸二异癸酯、木质素、凡士林和所述滤渣进行混合以制得塑木材料;3)将所述塑木材料混炼、挤出成型以制得所述环保型塑木复合板。2.根据权利要求1所述的制备方法,其中,在步骤1)中,所述芝麻杆、高粱杆的重量比为1:3-6。3.根据权利要求1所述的制备方法,其中,所述碱液的pH为10-12。4.根据权利要求3所述的制备方法,其中,所述芝麻杆、碱液的重量比为1:35-50。5.根据权利要求1所述的制备方法,其中,所述浸泡满足以下条件:浸泡温...
【专利技术属性】
技术研发人员:张三喜,张观兵,
申请(专利权)人:安徽爱瑞德新材料有限公司,
类型:发明
国别省市:安徽,34