A paint spraying and drying method includes the following steps: 1. degreasing, removing the oil stain on the surface of ferrous metal workpieces in the production process, using the trough immersion method; 2. cleaning; 3. rust removal, using acid rust removal, removing the rust scale on the surface of iron and steel, using the trough immersion method; 4. cleaning; 5. surface adjustment, used for surface treatment before phosphating. Use bath immersion method; 6. Phosphating, using zinc phosphating solution to phosphate the surface of steel, using bath immersion method; 7. Cleaning; 8. Drying; 9. Spraying. The method of painting spraying and drying of the invention has better spraying effect and is not easy to fall off through the bath immersion method and the matching of ingredients in the formula, and adopts special drying process, which prolongs the adhesion time in particular and reduces the use cost of mechanical equipment.
【技术实现步骤摘要】
一种油漆喷涂及烘干的方法
本专利技术涉及喷涂
，尤其涉及一种油漆喷涂及烘干的方法。
技术介绍
大部分机械设备都需要通过喷漆进行表面防滑和防腐蚀，从而延长整个设备的寿命，而传统的喷漆工艺知识将尤其直接喷涂与设备表面，造成容易脱落等问题，从而使设备更加容易受到腐蚀，缩短了使用寿命，增加了使用成本。
技术实现思路
为了克服传统喷涂工艺存在的上述问题，本专利技术提供了一种喷涂之后不易脱落的油漆喷涂及烘干的方法。本专利技术为实现上述目的所采用的技术方案是：一种油漆喷涂及烘干的方法，包括以下步骤：（1）除油，去除黑色金属工件在生产过程中表面的油污，用槽浸法；（2）清洗；（3）除锈，采用酸性除锈，去除钢铁表面的锈垢，用槽浸法；（4）清洗；（5）表调，用于磷化前的表面处理，用槽浸法；（6）磷化，用锌系磷化液使钢铁表面磷化，用槽浸法；（7）清洗；（8）干燥；（9）喷涂。所述步骤（1）中碱液清洗配方：氢氧化钠5%、磷酸钠5%、磷酸三钠5%、OP-10乳化液0.2%、温度93~98℃，处理时间8~10分钟。所述步骤（3）中酸洗除锈液配方：浓度42%的工业盐酸、缓蚀剂8%，温度：常温。...
【技术保护点】
1.一种油漆喷涂及烘干的方法，其特征在于：包括以下步骤：（1）除油，去除黑色金属工件在生产过程中表面的油污，用槽浸法；（2）清洗；（3）除锈，采用酸性除锈，去除钢铁表面的锈垢，用槽浸法；（4）清洗；（5）表调，用于磷化前的表面处理，用槽浸法；（6）磷化，用锌系磷化液使钢铁表面磷化，用槽浸法；（7）清洗；（8）干燥；（9）喷涂。
【技术特征摘要】
1.一种油漆喷涂及烘干的方法，其特征在于：包括以下步骤：（1）除油，去除黑色金属工件在生产过程中表面的油污，用槽浸法；（2）清洗；（3）除锈，采用酸性除锈，去除钢铁表面的锈垢，用槽浸法；（4）清洗；（5）表调，用于磷化前的表面处理，用槽浸法；（6）磷化，用锌系磷化液使钢铁表面磷化，用槽浸法；（7）清洗；（8）干燥；（9）喷涂。2.根据权利要求1所述的一种油漆喷涂及烘干的方法，其特征在于：所述步骤1中碱液清洗配方：氢氧化钠5%、磷酸钠5%、磷酸三钠5%、OP-10乳化液0.2%、温度93~98℃，处...
【专利技术属性】
技术研发人员：董春艳，
申请(专利权)人：合肥优亨旺信息科技有限公司，
类型：发明
国别省市：安徽,34
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。