The invention discloses an intelligent discoloring composite film under visible light and a preparation method thereof. The composite film is composed of membrane materials, silica nanoparticles and luminescent materials. The purpose of the composite film is to produce reversible stretching discoloration under visible light by introducing fluorescent dyes on the basis of the original stretching controllable light transmission film. The invention also provides a preparation method of the composite film. The prepared composite films have simple structure, excellent reversibility and high mechanical sensitivity. These properties make it widely used in smart glass, strain sensor, anti-counterfeiting of high-end luxury goods and so on.
【技术实现步骤摘要】
一种可见光照下智能变色复合膜及其制备方法
本专利技术属于复合材料领域，具体涉及一类智能变色材料，特别涉及在可见光照下可逆拉伸变色薄膜及其制备方法和用途。
技术介绍
在自然界，很多生物在受到外界刺激时会发生颜色或者透明度的改变，从而躲避天敌或者适应环境变化。例如比目鱼能够随着环境变化改变身体的颜色；章鱼等头足类动物为了伪装和通信能够立刻改变他们皮肤颜色和图案。仿照这种生物变色的机理，科研人员研制了各种新型、先进的智能变色材料。这些材料能够在光、热、电等外界刺激下发生形貌或者物质的变化从而产生颜色或者透明度的改变。美国康涅狄格大学SongshanZeng等人(ZengS,ZhangD,HuangW,etal.Bio-inspiredsensitiveandreversiblemechanochromismsviastrain-dependentcracksandfolds[J].NatureCommunications,2016,7:11802.)受到海洋生物的启发，利用形变控制表面结构的方法，设计了一种柔性衬底和刚性薄膜组成的混合双层材料体系，并通过拉伸使脆性薄膜表...
【技术保护点】
1.一种在可见光照下智能变色薄膜，其特征是，所述薄膜的组成成份是聚硅氧烷、荧光剂和SiO2纳米微球，其中聚硅氧烷/荧光剂复合层为第一层(1)，聚硅氧烷/荧光剂胶体填充SiO2纳米颗粒间隙，形成SiO2纳米颗粒嵌入的聚硅氧烷/荧光剂薄膜为第二层(2)，如图1所示；该薄膜在可见光下呈现出明显的橙黄色，通过拉伸变为粉红色，应变恢复时又变成了橙黄色，并且通过多次拉伸现象不变，具有良好可逆性。
【技术特征摘要】
1.一种在可见光照下智能变色薄膜，其特征是，所述薄膜的组成成份是聚硅氧烷、荧光剂和SiO2纳米微球，其中聚硅氧烷/荧光剂复合层为第一层(1)，聚硅氧烷/荧光剂胶体填充SiO2纳米颗粒间隙，形成SiO2纳米颗粒嵌入的聚硅氧烷/荧光剂薄膜为第二层(2)，如图1所示；该薄膜在可见光下呈现出明显的橙黄色，通过拉伸变为粉红色，应变恢复时又变成了橙黄色，并且通过多次拉伸现象不变，具有良好可逆性。2.如权利要求1所述的薄膜，其特征是：所述的聚硅氧烷为聚二甲基硅氧烷(PDMS)。3.如权利要求1所述的薄膜，其特征是：所述的发光材料为荧光剂。4.如权利要求1所述的薄膜，其特征是：所述的SiO2纳米微球为自制的100-350nmSiO2微球溶胶，其多分散性(PDI)小于5％。5.如权利要求4所述的SiO2纳米微球溶胶，其制备方法为：改进的Stober法制备SiO2纳米微球，在锥形瓶中按照一定比例配制浓氨水、乙醇、去离子水以及TEOS溶液搅拌均匀。封住瓶口后继续反应2h。反应在带有磁力搅拌的恒温水浴锅中进行。将反应得到的悬浮液进行离心清洗，...