一种大比表面积类石墨相碳化氮及其制备方法技术

本发明专利技术公开了一种大比表面积类石墨相碳化氮及其制备方法。其步骤如下，将密勒胺与叔丁硒基乙酸按照10～30:1的质量比，在400～600℃管式炉中，通氮气保护下煅烧2～4小时，即可得到大比表面积类石墨相碳化氮。与传统方法不掺杂硒制备的类石墨相碳化氮相比，添加硒助剂后制备的材料，比表面积增加10.2倍，因此带来更加优越的催化性能，具有较好的应用前景。

A large surface area graphite like phase carbonized nitrogen and its preparation method

The invention discloses a large surface area graphite like phase carbonized nitrogen and a preparation method thereof. The steps are as follows. Graphite-like nitrogen carbide with specific surface area can be obtained by calcination of melamine and tert-butylselenoacetic acid at a mass ratio of 10 to 30:1 in a tubular furnace at 400 to 600 degrees C for 2 to 4 hours under the protection of nitrogen. Compared with the graphite-like nitrogen carbide prepared by the traditional method without doping selenium, the specific surface area of the materials prepared by adding selenium additives increases by 10.2 times, which brings more superior catalytic performance and has better application prospects.

【技术实现步骤摘要】
一种大比表面积类石墨相碳化氮及其制备方法
本专利技术涉及一种制备大比表面积类石墨相碳化氮及其方法，属于催化剂材料制备领域。
技术介绍
类石墨相碳化氮是最近刚被专利技术的一种新型二维催化剂材料，它最著名的性能是可以在可见光照下分解水，因此，是新能源领域的研究热点之一。除此之外，类石墨相碳化氮还可以用于催化一些有机氧化反应，有重大的工业应用前景。而增加催化剂材料的比表面积，能够提高催化剂效率，是重要的催化剂制备技术。目前，制备大比表面积类石墨相碳化氮的方法不多，主要采取金属掺杂或者反复煅烧方法。前者会带入金属离子污染，而后者步骤繁琐，能耗较大。因此，开发更加简洁的，无金属掺杂的大比表面积类石墨相碳化氮的合成方法，有很好的应用价值。
技术实现思路
本专利技术的目的是提供一种大比表面积类石墨相碳化氮及其制备方法。本专利技术以密勒胺为原料，叔丁硒基乙酸为助剂，合成大比表面积类石墨相碳化氮；所述方法简单，具有较高的实际应用价值。为解决上述技术问题,本专利技术提供的技术方案是：一种大比表面积类石墨相碳化氮及其制备方法，在管式炉中按照质量比10～30:1的比例加入密勒胺与叔丁硒基乙酸，在氮气保护下，于4本文档来自技高网...

【技术保护点】
1.一种大比表面积类石墨相碳化氮的制备方法，其特征在于，按照质量比10～30:1的比例加入密勒胺与叔丁硒基乙酸，在氮气保护下，于400～600oC煅烧2～4小时，即可得到所述的大比表面积类石墨相碳化氮材料。

【技术特征摘要】
1.一种大比表面积类石墨相碳化氮的制备方法，其特征在于，按照质量比10～30:1的比例加入密勒胺与叔丁硒基乙酸，在氮气保护下，于400～600oC煅烧2～4小时，即可得到所述的大比表面积类石墨相碳化氮材料。2.如权利要求1所述的方法，其特征在于，密勒胺与叔丁硒基乙酸的质量比为10～30:1。3.如权利要求1所述的方法，其特征在于，密勒胺与叔丁硒基乙酸的质量比为20:1。4.如权利要求1所述的方...

【专利技术属性】
技术研发人员：俞磊，曹宽宏，邓鑫，
申请(专利权)人：扬州大学，
类型：发明
国别省市：江苏,32