The invention discloses a coating technology for improving the service life of gear hobbing cutter, which dries and mixes tungsten metal powder, carbon powder, silicon powder, manganese powder, titanium powder and copper metal powder, sprays metal powder mixture evenly on the surface of the heated gear hobbing cutter, puts the hobbing cutter into the container, adds inert gas and adds it. Heat, sintering, sintering three layers of metal mixture; after cooling, gear processing hobbing cutter. Compared with the prior art, the surface of the hobbing cutter is sintered by the prescription and processing technology of the present invention, so that the surface hardness of the hobbing cutter is improved, the wear resistance of the hobbing cutter is improved, and the service life of the hobbing cutter is improved, which has the value of popularization and application.
【技术实现步骤摘要】
一种提高齿轮加工滚齿刀寿命的涂层工艺
本专利技术涉及一种金属加工工艺，尤其涉及一种提高齿轮加工滚齿刀寿命的涂层工艺。
技术介绍
滚切齿轮属于展成法，可将看作无啮合间隙的齿轮与齿条传动。当滚齿刀旋转一周时，相当于齿条在法向移动一个刀齿，滚刀的连续传动，犹如一根无限长的齿条在连续移动。当滚刀与滚齿坯间严格按照齿轮与齿条的传动比强制啮合传动时，滚刀刀齿在一系列位置上的包络线就形成了工件的渐开线齿形。随着滚刀的垂直进给，即可滚切出所需的渐开线齿廓。现有技术中，滚齿刀的硬度较低，且表面不耐磨，从而导致了滚齿刀的使用寿命较低，因此，存在改进空间。
技术实现思路
本专利技术的目的就在于为了解决上述问题而提供一种提高齿轮加工滚齿刀寿命的涂层工艺。本专利技术通过以下技术方案来实现上述目的：本专利技术包括以下步骤：（1）将钨金属粉末、碳粉、硅粉、锰粉、钛粉、铜金属粉进行干燥混合；（2）将齿轮加工滚齿刀置入容器中，加入惰性气体，并加热至1000℃-1200℃；（3）将步骤（1）混合的金属粉混合物均匀喷涂于步骤（2）加热的齿轮加工滚齿刀表面进行烧结；（4）进行缓慢降温至400℃-500℃，保...
【技术保护点】
1.一种提高齿轮加工滚齿刀寿命的涂层工艺，其特征在于，包括以下步骤：将钨金属粉末、碳粉、硅粉、锰粉、钛粉、铜金属粉进行干燥混合；将齿轮加工滚齿刀置入容器中，加入惰性气体，并加热至1000℃‑1200℃；将步骤（1）混合的金属粉混合物均匀喷涂于步骤（2）加热的齿轮加工滚齿刀表面进行烧结；进行缓慢降温至400℃‑500℃，保温10min；再次升温至1000℃‑1200℃，重复步骤（3）和步骤（4）三次，烧结三层金属混合物；待冷却后制得齿轮加工滚齿刀。
【技术特征摘要】
1.一种提高齿轮加工滚齿刀寿命的涂层工艺，其特征在于，包括以下步骤：将钨金属粉末、碳粉、硅粉、锰粉、钛粉、铜金属粉进行干燥混合；将齿轮加工滚齿刀置入容器中，加入惰性气体，并加热至1000℃-1200℃；将步骤（1）混合的金属粉混合物均匀喷涂于步骤（2）加热的齿轮加工滚齿刀表面进行烧结；进行缓慢降温至400℃-500℃，保温10min；再次升温至1000℃-1200℃，重复步骤（3）和步骤（4）三次，烧结三层金属混合物；待冷却后制得齿轮...