The invention discloses a backwater pressure waterproof coating for backwater surface leak plugging and seepage resistance and its preparation method, which comprises the following substances by weight: 400 500 Portland cement, 350 480 sand fillers, 20 50 latex powder, 5 10 waterproof agent, 10 50 coagulant, 20 50 active masterbatch, 2 10 thixotropic agent, etc. Ingredients: fiber 2, 5, cellulose ether 0, 2, defoamer 1, 3, pigment 1, 10. The backwater pressure waterproof coating for backwater leakage and seepage prevention has strong bonding with the base surface, high flexural and compressive strength, good impermeability, excellent aging resistance, long service life, low shrinkage and absorption rate, and excellent waterproof performance.
【技术实现步骤摘要】
用于背水面堵漏抗渗的背水压防水涂料及其制备方法
本专利技术涉及建筑防水材料领域，特别地，本专利技术涉及一种用于背水面堵漏抗渗的背水压防水涂料及其制备方法。
技术介绍
房屋、地下室、市政工程等建筑，由于建筑主体多为混凝土结构，混凝土在凝固过程中，容易出现毛细孔和收缩缝，若前期防水工程做的不够完善，或者出现防水层破坏、管线损坏、新产生墙体裂缝等，都会导致建筑物出现渗漏。而通常后期出现渗漏，一般都采用背水面堵漏方式。现今背水面堵漏采用较多的是“灌浆堵漏”。灌浆堵漏，通过在渗漏裂缝处，进行钻孔埋设灌浆嘴，使用高压灌浆机，将聚氨酯、环氧树脂等灌浆堵漏剂，高压灌入到混凝土内部，从而填充裂缝，以达到堵漏目的。但是，用灌浆堵漏，通常存在以下技术问题：(1)材料易老化且粘结性不够：灌浆材料，一般是有机反应物，时间长易出现老化损坏现象，且与混凝土等无机基材粘结相对于水泥基材料较差；(2)适用范围窄：在渗漏点或裂缝明显情况下适用；(3)施工方法难度大：在探查出渗漏点或裂缝后，需要合理设计布孔方案，选择合适的灌浆孔，然后钻墙打孔，固定灌浆嘴，利用高压灌浆机将灌浆堵漏剂灌入到混凝土内部；需...
【技术保护点】
1.一种用于背水面堵漏抗渗的背水压防水涂料，其特征在于，按重量份数计，包括以下物质：硅酸盐水泥400‑500份；砂填料350‑480份；乳胶粉20‑50份；防水剂5‑10份；促凝剂10‑50份；活性母料20‑50份；触变剂2‑10份；纤维2‑5份；纤维素醚0‑2份；消泡剂1‑3份；颜料1‑10份。
【技术特征摘要】
1.一种用于背水面堵漏抗渗的背水压防水涂料，其特征在于，按重量份数计，包括以下物质：硅酸盐水泥400-500份；砂填料350-480份；乳胶粉20-50份；防水剂5-10份；促凝剂10-50份；活性母料20-50份；触变剂2-10份；纤维2-5份；纤维素醚0-2份；消泡剂1-3份；颜料1-10份。2.根据权利要求1所述的用于背水面堵漏抗渗的背水压防水涂料，其特征在于，所述硅酸盐水泥为P.W52.5级白水泥。3.根据权利要求1所述的用于背水面堵漏抗渗的背水压防水涂料，其特征在于，所述砂填料为粒径范围为0.15mm-0.40mm的石英砂和/或钙砂。4.根据权利要求1所述的用于背水面堵漏抗渗的背水压防水涂料，其特征在于，所述乳胶粉为苯丙胶粉、丁苯胶粉、VAE胶粉中的一种或多种。5.根据权利要求1所述的用于背水面堵漏抗渗的背水压防水涂料，其特征在于，所述防水剂为憎水型硅烷基粉末和/或硬脂酸盐防水剂。6.根据权利要求...
【专利技术属性】
技术研发人员：刘剑洪，龚兴宇，黄莉恒，
申请(专利权)人：南通科顺建筑新材料有限公司，
类型：发明
国别省市：江苏,32