一种高浓度稀土掺杂碲钨镧玻璃及其制备方法技术

一种碲钨镧玻璃及其制备方法，该玻璃的摩尔百分比组成范围为：二氧化碲:百分之六十五至七十；三氧化钨：百分之十五至二十；氧化镧：百分之十至十五；氧化铒：百分之零至四。采用刚玉坩埚和硅钼棒电炉熔融方法制备。经测试证明：该玻璃的转变温度在450‑473℃，玻璃稳定性好，稀土离子掺杂浓度高，可达4 mol%，且获得较强的2.7μm发光，说明该玻璃适合作为中红外发光的基质材料。

High concentration rare earth doped tellurium tungsten lanthanum glass and preparation method thereof

A lanthanum tellurium glass and its preparation method. The molar percentage composition of the glass ranges from: tellurium dioxide: 65 to 70 percent; tungsten trioxide: 15 to 20 percent; lanthanum oxide: 10 to 15 percent; and erbium oxide: 0 to 4 percent. The corundum crucible and silicon molybdenum rod melting method were adopted. The test results show that the glass has good stability at 450 473 (?) C, high doping concentration of rare earth ions, up to 4 mol%, and strong 2.7 um luminescence, which indicates that the glass is suitable for mid-infrared luminescence.

【技术实现步骤摘要】
一种高浓度稀土掺杂碲钨镧玻璃及其制备方法
本专利技术涉及一种高浓度稀土掺杂碲钨镧玻璃及其制备方法。
技术介绍
碲酸盐玻璃有着高折射率、高介电常数和宽的红外透过范围等性能，作为近-中红外玻璃基质材料多年来一直受到人们的注意。大量的研究均表明这种玻璃结构中的稀土离子具有较好的发光性能，适合于做稀土发光的基质材料，因此被认为是一种优良的中红外发光的基质材料。在碲酸盐玻璃中研究较多的系统为TeO2–ZnO-Na2O（TZN）和TeO2–WO3–La2O3（TWL）两个体系。在这两个体系中，均可实现低声子能量和高折射率的性能，但比较而言，TZN系统的转变温度低于300℃，而TWL稀土的转变温度可高于400℃，不利于TZN系统在光纤材料中获得高功率输出和较好的光学质量。从未来稀土掺杂碲酸盐玻璃使用角度考虑，TWL系统有着更为广泛的应用。因此，在前人研究基础上探索稀土离子掺杂浓度高、抗析晶稳定性好的新型TWL玻璃是非常有意义的。
技术实现思路
本专利技术要解决的技术问题在于提供一种碲钨镧玻璃，该玻璃具有优良的抗析晶稳定性能、高稀土掺杂浓度和良好的透过性能，在980nm波长的激光二极管泵浦下能获得很强的本文档来自技高网...

【技术保护点】
1.一种碲钨镧玻璃，其特征在于它的摩尔百分比组成为：组成                           mol％TeO2                           65～70，WO3                            15～20,La2O3                          10～15，Er2O3                           0～4。

【技术特征摘要】
1.一种碲钨镧玻璃，其特征在于它的摩尔百分比组成为：组成mol％TeO265～70，WO315～20,La2O310～15，Er2O30～4。2.根据权利要求1所述的碲钨镧玻璃，其特征在于所述的玻璃透过率高，热稳定性好。3.根据权利要求1所述的碲钨镧玻璃，其特征在于所述玻璃的稀土离子掺杂浓度高，且中红外发光强度高。4.根据权利要求1所述的碲钨镧玻璃的制备方法，包括下列步骤：①选定所述的玻璃组成及其摩尔百分...

【专利技术属性】
技术研发人员：郭艳艳，刘秀玲，杨永硕，
申请(专利权)人：长春理工大学，
类型：发明
国别省市：吉林,22