The invention relates to a sandwich structure metal composite negative plate for secondary batteries, which comprises M metal sheet and metal nanowire layer adhering to the upper and lower surfaces of M metal sheet. The M metal sheet is lithium metal sheet, sodium metal sheet or magnesium metal sheet. The metal nanowire layer consists of a group of metal nanowires adhering to the surface of M metal sheet. The metal nanowires are copper nanowires, nickel nanowires or copper nickel nanowires. The advantages of the invention are that the surface current is dispersed by the network structure formed by the metal nanowires adhering to the upper and lower surfaces of the M metal sheet, and the distribution of M metal ions is more uniform.
【技术实现步骤摘要】
一种二次电池用三明治结构金属复合负极片
本专利技术涉及一种二次电池用三明治结构金属复合负极片，特别是一种三明治结构锂金属复合负极片，属于二次电池
技术介绍
据了解，相比于现有商业应用二次电池，例如锂离子电池中的石墨负极，锂金属负极理论上可以提供更多的容量(3860mAh·g-1)和最负的电势(-3.040Vvs.标准氢电极)，锂金属负极有望在下一代便携式电子设备以及电动汽车等领域实现较大的应用。然而，自1970年代第一代商业锂金属全电池问世不久就出现了爆炸事故，这是因为当锂作为电池负极时，在循环过程中金属锂在平整锂片表面沉积时，由于尖端沉积效应后续沉积的锂会沿着先沉积的锂生长，进而形成锂枝晶。由于枝晶锂的产生，部分枝晶锂脱离锂基底而成为“死锂”，无法再被利用，枝晶锂持续生长堆积会刺破隔膜造成电池短路，死锂增多会导致更多的锂不能再参与电池利用造成库伦效率降低，容量不可逆的损失。这些都将会造成锂金属电池的寿命和安全性问题。因此，如何调控锂表面的结构，促使电流和锂离子在负极表面均匀分布是如今需要重点研究的热点问题。
技术实现思路
本专利技术的目的在于：针对现有技术...
【技术保护点】
1.一种二次电池用三明治结构金属复合负极片，其特征在于：包括M金属片和粘附在M金属片上、下表面的金属纳米线层，所述M金属片为锂金属片、钠金属片或镁金属片，所述金属纳米线层由一组粘附在M金属片表面的金属纳米线组成，所述金属纳米线为铜纳米线、镍纳米线或铜镍纳米线。
【技术特征摘要】
1.一种二次电池用三明治结构金属复合负极片，其特征在于：包括M金属片和粘附在M金属片上、下表面的金属纳米线层，所述M金属片为锂金属片、钠金属片或镁金属片，所述金属纳米线层由一组粘附在M金属片表面的金属纳米线组成，所述金属纳米线为铜纳米线、镍纳米线或铜镍纳米线。2.根据权利要求1所述一种二次电池用三明治结构金属复合负极片，其特征在于：所述M金属片为锂金属片，所述金属纳米线为铜纳米线。3.根据权利要求1所述一种二次电池用三明治结构金属复合负极片，其特征在于：所述金属纳米线的粘附方式为加压复合。4.根据权利要求2所述一种二次电池用三明治结构金属复合负极片，其特征在于：所述锂金属片的厚度为10～500μm。5.根据权利要求2所述一种二次电池用三明治结构金属复合负极片，其特征在于：所述铜纳米线的直径为50～100nm，长度为50～200μm。6.根据权利要求1所述一种二次电...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。