The invention discloses a preparation method of NbTi superconductor with high current and high stability. The NbTi/Cu multi-core superconductor circular wire is hot-tinned to uniformly coat the surface with a Sn_5% Cu alloy, and then stranded to form a multi-strand conductor. Sn 5% Cu alloy thin strips are wound on the surface of multi-stranded conductors by winding equipment, then placed in special-shaped copper groove wires. The two strips are inlaid together by rolling. The critical current of NbTi/Cu superconductor with high copper ratio prepared by the method of the invention is greater than 10000 A and the RRR value is greater than 100, which meets the requirements of high energy magnet for high copper ratio and high working current.
【技术实现步骤摘要】
一种高电流高稳定性NbTi超导体制备方法
本专利技术属于超导线材加工
，涉及一种高电流高稳定性NbTi超导体制备方法。
技术介绍
高能超导磁体因储存着较高的能量，承载着较高的电流，电流达到万安级。超导体中热扰动可通过铜基体转移到冷却媒介中，减少了磁体失超的风险。因此应磁体运行稳定性的要求，高能超导磁体需要大铜比的超导缆。而由超导线直接绞成的超导缆铜比一般不大于7，该铜比较低，不能满足使用需求。超导缆由多股超导线材绞制成，铜槽线由铜棒直接加工而成，将超导缆镶嵌到铜槽线中相对简单，在保证大电流的条件下，铜比大大升高，且能够满足高能超导磁体高电流、高铜比稳定性的需求，适用于高能超导磁体，具有高工作电流、低交流损耗、高稳定性等特点。高能超导磁体中最常用的是NbTi超导体，目前NbTi超导体主要应用于磁共振成像(MRI)、核磁共振(NMR)、实验室仪器、粒子加速器、电力、扫雷、矿石磁分离、磁悬浮列车、超导储能(SMES)等领域。目前全世界需使用NbTi超导线约3600吨，而其中高铜比超导线材所占比例约为80％，NbTi超导线材的制备和批量生产成为重中之重。若能将NbT...
【技术保护点】
1.一种高电流高稳定性NbTi超导体制备方法，其特征在于，具体包括以下步骤：步骤1，将NbTi/Cu多芯超导圆线进行热镀锡，使表面均匀涂覆一层Sn‑5％Cu合金；步骤2，将表面覆锡后的NbTi/Cu多芯超导圆线绞制成多股导体，并加工槽宽和槽深与导体尺寸相匹配的异型铜槽线；步骤3，采用绕包设备将Sn‑5％Cu合金薄条缠绕在步骤2中的多股导体表面上；步骤4，将绕包锡薄条后的导体置于异型铜槽线中，采用轧制的方式将二者镶嵌到一起，之后在管式真空感应炉中进行加热，将锡薄条完全融化从而使导体和铜槽线完全结合到一起。
【技术特征摘要】
1.一种高电流高稳定性NbTi超导体制备方法，其特征在于，具体包括以下步骤：步骤1，将NbTi/Cu多芯超导圆线进行热镀锡，使表面均匀涂覆一层Sn-5％Cu合金；步骤2，将表面覆锡后的NbTi/Cu多芯超导圆线绞制成多股导体，并加工槽宽和槽深与导体尺寸相匹配的异型铜槽线；步骤3，采用绕包设备将Sn-5％Cu合金薄条缠绕在步骤2中的多股导体表面上；步骤4，将绕包锡薄条后的导体置于异型铜槽线中，采用轧制的方式将二者镶嵌到一起，之后在管式真空感应炉中进行加热，将锡薄条完全融化从而使导体和铜槽线完全结合到一起。2.根据权利要求1所述的高电流高稳定性NbTi超导体制备方法，其特征在于，所述步骤1中，锡液的加热温度为300～320℃，热镀锡速度为80-120m/mi...
【专利技术属性】
技术研发人员：郭强，张平祥，李建峰，朱燕敏，闫凯鹃，柳祥，刘建伟，刘向宏，冯勇，