The invention relates to a method for preparing tin dioxide and zinc oxide heterojunction nanoflowers in solid state, belonging to the field of preparation of nanomaterials. In this method, tin tetrachloride, zinc acetate and sodium hydroxide were mixed and ground at room temperature to synthesize tin dioxide-zinc oxide heterojunction nanoflowers in low-temperature solid state. The low-temperature solid-phase chemical method for preparing tin dioxide-zinc oxide heterojunction nanoflowers has the advantages of simple operation, no solvent, high yield, low cost and simple synthesis process, and the tin dioxide-zinc oxide heterojunction nanoflowers prepared by the invention have large specific surface area and high reaction activity, and will be photoelectric. Devices, photocatalysis and other fields have potential applications.
【技术实现步骤摘要】
一种固相制备二氧化锡-氧化锌异质结纳米花的方法
本专利技术涉及一种固相制备二氧化锡-氧化锌异质结纳米花的方法，属于纳米材料制备领域。
技术介绍
近年来，纳米材料由于其本身所具有的独特的物理化学特性而受到了科研工作者的广泛关注。硫化锌作为一种十分重要的半导体纳米材料，因其具有特异的光、电、热、磁等性质，而在半导体发光器件、非线性光学材料、光催化等领域表现出巨大的应用前景。然而，其光生电子和空穴复合较快，因而需要对其进行改性研究。由于氧化锌和二氧化锡合适的能带结构，使二氧化锡-氧化锌异质结显示出巨大优势。三维纳米结构与纳米粉体不同，不仅具有小尺寸效应、表面效应、量子尺寸效应等特殊性质，又存在由纳米结构组合引起的新的量子耦合效应和协同效应等，显示出优异的光学、电学性能，因而二氧化锡-氧化锌异质结纳米花具有更明显的潜在应用。目前，制备二氧化锡-氧化锌异质结纳米花的方法包括水热法和微波法等，然而这些方法涉及到实验条件苛刻、能耗高等不足，因而开发一种简单、高产、环境友好的合成方法仍然十分迫切。低热固相化学法具有操作简单、成本低、产量高和环境友好等优点，已经成为合成纳米材料的一种有效方法。
技术实现思路
本专利技术的目的在于提供一种二氧化锡-氧化锌异质结纳米花的制备方法，利用二者独特的能带结构，采用低热固相化学反应来制备二硫化钼-硫化锌异质结纳米材料。该方法克服了二氧化锡纳米材料在制备过程中发生严重团聚现象，并实现了二氧化锡与氧化锌的复合。本专利技术公开了一种固相制备二氧化锡-氧化锌异质结纳米花的方法。本专利技术是将四氯化锡、醋酸锌和氢氧化钠作为反应物，在室温下通过研磨发生...
【技术保护点】
1.一种固相制备二氧化锡‑氧化锌异质结纳米花的方法，其特征是适量四氯化锡置于玛瑙研钵中，研细后加入十二烷基硫酸钠，研磨后加入适量醋酸锌，研磨后加入氢氧化钠，再充分研磨并放置完成固相反应，用去离子水和无水乙醇洗涤，抽滤，在干燥箱中60度干燥2小时制得二氧化锡‑氧化锌异质结纳米花。
【技术特征摘要】
1.一种固相制备二氧化锡-氧化锌异质结纳米花的方法，其特征是适量四氯化锡置于玛瑙研钵中，研细后加入十二烷基硫酸钠，研磨后加入适量醋酸锌，研...