The invention relates to a mesoporous copper-based alumina catalyst, its preparation method and application. The preparation method includes: dissolving copper source and template in organic solvent to obtain precursor solution; dissolving aluminium source and acid in organic solvent to obtain carrier solution; mixing, stirring and aging the precursor solution and carrier solution. The mesoporous copper based alumina catalyst was obtained by calcining and calcining. The mesoporous copper-based alumina catalyst has the advantages of good activity, high selectivity, high strength, easy separation, homogeneous catalyst particles, easy activation, etc. The preparation method of the catalyst is simple, feasible, good repeatability, and remarkable economic and technical performance.
【技术实现步骤摘要】
介孔铜基氧化铝催化剂、制备方法及应用
本专利技术涉及一种催化剂制备领域，特别是涉及一种介孔铜基氧化铝催化剂、制备方法及其应用。
技术介绍
随着世界经济的发展，纺织、医药、化工、汽车工业等领域快速发展，作为其中重要原料的1，4-丁二醇的需求量也逐年增加。生产1，4-丁二醇有石油和煤炭两条路线。前者以丁烷法和丁烯法为代表，该类方法路线较为繁琐，但能耗较低，适合以石油为主要资源的国家进行生产；后者指炔醛法，该方法路线简单，转化率和产率较高，但能耗较高，适合煤炭资源丰富的国家和地区采用。我国具有丰富的煤炭资源，通过炔醛法工艺制备1，4-丁二醇具有得天独厚的优势，所以我国制备1，4-丁二醇以乙炔甲醛化合成路线为主。目前，制备1，4-丁二醇分两步，一是甲醛和乙炔反应合成1，4-丁炔二醇，而是1，4-丁炔二醇加氢制备1，4-丁二醇。在合成1，4-丁炔二醇反应中，以甲醛和乙炔为原料，采用铜基催化剂。在反应过程中，Cu2+先被HCHO还原Cu+，然后Cu+与乙炔相互作用生成炔铜络合物活性中心。目前，工业上采用的铜基催化剂分为无载体型催化剂和负载型催化剂。无载体型催化剂包括孔雀石、含...
【技术保护点】
1.一种介孔铜基氧化铝催化剂的制备方法，其特征在于，其包括：将铜源和模板剂溶于有机溶剂中，得到前驱体溶液；将铝源和酸溶于有机溶剂中，得到载体溶液；将所述的前驱体溶液和载体溶液混合，搅拌，老化，煅烧，得到介孔铜基氧化铝催化剂。
【技术特征摘要】
1.一种介孔铜基氧化铝催化剂的制备方法，其特征在于，其包括：将铜源和模板剂溶于有机溶剂中，得到前驱体溶液；将铝源和酸溶于有机溶剂中，得到载体溶液；将所述的前驱体溶液和载体溶液混合，搅拌，老化，煅烧，得到介孔铜基氧化铝催化剂。2.根据权利要求1所述的介孔铜基氧化铝催化剂的制备方法，其特征在于，所述的载体溶液中还包括铋盐；所述的铋盐为硝酸铋、硫酸铋和醋酸铋中的至少一种。3.根据权利要求1所述的介孔铜基氧化铝催化剂的制备方法，其特征在于，所述的铜源为乙酰丙酮铜、硝酸铜、硫酸铜和醋酸铜中的至少一种；所述的模板剂为P123或F127；所述的铝源为异丙醇铝、异丁醇铝、仲丁醇铝和三异丙醇铝中的至少一种；所述的酸为硝酸、硫酸或醋酸；所述的有机溶剂为乙醇、甲醇或丙酮。4.根据权利要求1所述的介孔铜基氧化铝催化剂的制备方法，其特征在于，所述的搅拌时间为5-12h；所述的老化温度为50-80℃，老化时间为1-3d；所述的煅烧温度为400-1200℃，升温速率为0.5-5℃/min，煅烧时间为4-6h。5.根据权利要求1所述的介孔铜基氧化铝催化剂的制备方法，其特征在于，...
【专利技术属性】
技术研发人员：代斌，柳赛锋，彭文才，
申请(专利权)人：石河子大学，
类型：发明
国别省市：新疆,65