The invention discloses an environment-friendly Fiberboard Based on modified liquid paraffin and a processing method thereof. The processing method comprises the following steps: processing of modified liquid paraffin: mixing the paraffin emulsion, acrylic acid, OP 10 emulsifier and potassium persulfate, and heating and stirring to obtain modified liquid paraffin; and processing the environmental protection fiberboard: Plants. Fiber, modified liquid paraffin, bamboo chips, wheat bran, urea-formaldehyde resin, latex, PPE wet strength agent, penetrant, and water are mixed to get the size; the size through hot-pressing molding process to get environmental protection fiberboard; solve the current fiberboard there are still many shortcomings.
【技术实现步骤摘要】
基于改性液体石蜡的环保纤维板及其加工方法原案申请号：2017105778624。原案申请日：2017年7月15日。
本专利技术涉及纤维板加工领域，具体地，涉及一种基于改性液体石蜡的环保纤维板及其加工方法。
技术介绍
纤维板又名密度板，是以木质纤维或其他植物素纤维为原料，施加脲醛树脂或其他适用的胶粘剂制成的人造板，制造过程中可以施加胶粘剂和/或添加剂，纤维板具有材质均匀、纵横强度差小、不易开裂等优点，用途广泛。但是目前的纤维板还存在诸多不足之处，一是强度相对较低，二是吸水后容易膨胀变形。因此，提供一种强度较高，且具备优良的耐水性的环保纤维板及其加工方法是本专利技术亟需解决的问题。
技术实现思路
本专利技术的目的是提供一种基于改性液体石蜡的环保纤维板及其加工方法，解决了目前的纤维板还存在诸多不足之处，一是强度相对较低，二是吸水后容易膨胀变形的问题。为了实现上述目的，本专利技术提供了一种基于改性液体石蜡的环保纤维板的加工方法，所述加工方法包括：（1）改性液体石蜡的加工：将石蜡乳液、丙烯酸、OP-10乳化剂、过硫酸钾混合后进行加热搅拌，得到改性液体石蜡；（2）环保纤维板的加工...
【技术保护点】
1.一种基于改性液体石蜡的环保纤维板的加工方法，其特征在于，所述加工方法包括：（1）改性液体石蜡的加工：将石蜡乳液、丙烯酸、OP‑10乳化剂、过硫酸钾混合后进行加热搅拌，得到改性液体石蜡；（2）环保纤维板的加工：将植物纤维、改性液体石蜡、竹屑、麦麸、脲醛树脂、乳胶、PPE湿强剂、渗透剂、和水混合后得到浆料；（3）将浆料经热压成型工艺得到环保纤维板；其中，相对于100重量份的石蜡乳液，丙烯酸的用量为12‑25重量份，OP‑10乳化剂的用量为2‑5重量份，过硫酸钾的用量为3‑7重量份；相对于100重量份的植物纤维，改性液体石蜡的用量为15‑25重量份，竹屑的用量为10‑20重量...
【技术特征摘要】
1.一种基于改性液体石蜡的环保纤维板的加工方法，其特征在于，所述加工方法包括：（1）改性液体石蜡的加工：将石蜡乳液、丙烯酸、OP-10乳化剂、过硫酸钾混合后进行加热搅拌，得到改性液体石蜡；（2）环保纤维板的加工：将植物纤维、改性液体石蜡、竹屑、麦麸、脲醛树脂、乳胶、PPE湿强剂、渗透剂、和水混合后得到浆料；（3）将浆料经热压成型工艺得到环保纤维板；其中，相对于100重量份的石蜡乳液，丙烯酸的用量为12-25重量份，OP-10乳化剂的用量为2-5重量份，过硫酸钾的用量为3-7重量份；相对于100重量份的植物纤维，改性液体石蜡的用量为15-25重量份，竹屑的用量为10-20重量份，麦麸的用量为10-20重量份，脲醛树脂的用量为2-8重量份，乳胶的用量为1-...