The invention discloses a copper-titanium oxide composite photocatalyst, which forms a copper-titanium oxide Schottky junction by depositing elemental copper on the surface of a titanium dioxide nanosheet; the copper-titanium oxide composite photocatalyst has a mass ratio of 0.1:1; the copper-titanium oxide composite photocatalyst is in sheet shape with a length of 0.5_2 microns and a thickness of 0.5_2 microns. It is 30 100 nm. The present invention deposits copper on titanium dioxide nanosheets with {001} crystal surface as the main exposure surface by a simple in-situ reduction method, and obtains Cu_TiO2 Schottky junction with superior performance. Compared with TiO2 photocatalyst, the Cu_TiO2 Schottky junction synthesized by us greatly improves the photocatalytic activity. The preparation method is simple, the cost is low, and it has a good application prospect.
【技术实现步骤摘要】
一种新型铜-氧化钛复合光催化剂及其制备方法与应用
本专利技术涉及一种新型铜-氧化钛复合光催化剂及其简易制备方法、以及光催化活性。
技术介绍
进入21世纪，人类面临着能源和环境两个非常严峻的问题，特别是有毒且难降解有机污染物(如多环芳烃、多氯联苯、农药、染料等)引起的环境问题，已成为影响人类生存与健康的重大问题。利用半导体氧化物材料在太阳光照射下表面能受激活化的特性，可有效地氧化分解有机污染物。与传统的净化环境处理方法相比，半导体光催化技术拥有反应条件温和、无二次污染、操作简单和降解效果显著等优势。自光催化技术开发以来，研究和应用最多的光催化剂是TiO2。但其产生的光生电子空穴对很容易复合，导致电子和空穴不能及时迁移至表面参与氧化还原反应，从而光转化效率较低。因此，制备高活性的光催化剂，至关重要。由于铜是一种无毒的廉价金属，近年来在光催化剂的制备上，日益取代含铅、锑、镉、汞等有毒元素的化合物，如CuO，Cu2O等。近年来，TiO2纳米片由于其独特的片状形貌，引起了广泛的关注。但是其电子空穴对的分离效率仍然不高，因此，与能促进电子定向流动的金属材料复合，是一种非常有效...
【技术保护点】
1.一种新型铜‑氧化钛复合光催化剂，其特征在于：所述光催化剂通过在TiO2纳米片表面沉积单质铜，形成Cu‑TiO2肖特基结；所述单质铜的沉积量与氧化钛的质量比为0.1：1；所述铜‑氧化钛复合光催化剂整体呈片状，片状边长为0.5‑2微米，厚度为30‑100纳米。
【技术特征摘要】
1.一种新型铜-氧化钛复合光催化剂，其特征在于：所述光催化剂通过在TiO2纳米片表面沉积单质铜，形成Cu-TiO2肖特基结；所述单质铜的沉积量与氧化钛的质量比为0.1：1；所述铜-氧化钛复合光催化剂整体呈片状，片状边长为0.5-2微米，厚度为30-100纳米。2.权利要求1所述铜-氧化钛复合光催化剂的制备方法，其特征在于：具体步骤如下：将0.5g的40wt%氢氟酸加入30g冰醋酸，搅拌30分钟；再加入1.71g的钛酸四丁酯，搅拌0.5小时；然后，转移到聚四氟乙烯内衬高压釜中，180℃恒温水热反应24小时；离心、洗涤、干燥，600℃煅烧2小时，得到{001}晶面为主要暴露面的片状TiO2;将0.16mmol的五水合硫酸铜和步骤（1）中制备得到的片状二氧化钛，加入到30mL乙二醇中，搅拌10分钟；再加入...
【专利技术属性】
技术研发人员：滕飞，汤茂源，顾文浩，滕怡然，杨晋宇，
申请(专利权)人：南京信息工程大学，
类型：发明
国别省市：江苏,32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。