The invention relates to a preparation method of photocatalyst loaded with titanium dioxide nanowires. Firstly, titanium dioxide nanowires are prepared by P25 and NaOH, and then the prepared titanium dioxide nanowires are added to titanium trichloride (TiCl3) and ammonia NH3 H2O to prepare the composite titanium dioxide nanowires @ titanium dioxide NWs by hydrothermal method. The invention provides a cheap and efficient photocatalyst by preparing at 400 degree temperature. The composite TiO2NPs@TiO2NWs photocatalyst of the present invention has very good photocatalytic degradation performance, and can be rapidly degraded under normal temperature, atmospheric pressure and light, and has persistent photocatalytic activity.
【技术实现步骤摘要】
一种TiO2纳米线上负载TiO2纳米颗粒的光催化剂的制备方法
本专利技术涉及一种TiO2纳米线上负载TiO2纳米颗粒的光催化剂的制备方法，属于光催化剂
技术介绍
作为一种绿色催化剂，光催化剂近年来取得了巨大进展。推动光催化反应研究的巨大动力来源于清洁生产﹑能源危机﹑环境保护的强烈要求，以及光催化剂本身潜在的探索价值和应用潜力。一维TiO2异质结催化剂的高效催化降解能力可以让绝大部分污染物化为无害物质，为保护水资源做出贡献，可以一并解决国家和企业排放污水的问题。通过简单的水热反应制备TiO2纳米线，然后以制备好的纳米线为载体在水热过程中负载TiO2纳米颗粒，从而制备成一维TiO2纳米异质结构，再通过调控TiO2纳米颗粒的比例制备出性能最佳的产品。整个实验简单易行且环保无污染。通过将TiO2纳米颗粒负载在TiO2纳米线上，不但使产品保留了各自的性能，而且很大程度上增加了材料的比表面积，异质结界面也很大程度地促进了光生电荷与光生空穴的分离率，这些新性质对于提高催化剂的催化活性都是必不可少的。
技术实现思路
本专利技术的目的是提供一种TiO2纳米线上负载TiO2纳米...
【技术保护点】
1.一种TiO2纳米线上负载TiO2纳米颗粒的光催化剂的制备方法，制备步骤如下：(1)将P25型纳米二氧化钛溶解于NaOH溶液中，在170～190℃下进行水热反应24～48h，冷却后，过滤得固态物质，将固态物质加入到HCl溶液中进行离子交换，再过滤得固态物质，然后在400℃下煅烧5h，制得TiO2纳米线单体催化剂；(2)将TiCl3溶解于水中，再将步骤(1)制得的TiO2纳米线单体催化剂加入到此溶液中，再加入NH3·H2O，充分混合后转在180℃进行水热反应12h，冷却后，离心得固态物质，然后在400℃下煅烧2h，制得TiO2纳米线上负载TiO2纳米颗粒的光催化剂。
【技术特征摘要】
1.一种TiO2纳米线上负载TiO2纳米颗粒的光催化剂的制备方法，制备步骤如下：(1)将P25型纳米二氧化钛溶解于NaOH溶液中，在170～190℃下进行水热反应24～48h，冷却后，过滤得固态物质，将固态物质加入到HCl溶液中进行离子交换，再过滤得固态物质，然后在400℃下煅烧5h，制得TiO2纳米线单体催化剂；(2)将TiCl3溶解于水中，再将步骤(1)制得的TiO2纳米线单体催化剂加入到此溶液中，再加入NH3·H2O，充分混合后转在180℃进行水热反应12h，冷却后，离心得固态物质，然后在400℃下煅烧2h，制得Ti...