The invention discloses a waterproof and anticorrosion coating belonging to a chemical coating for waterproof and anticorrosion in the construction industry. It consists of asphalt as the main raw material, adding a small amount of acidifier maleic anhydride, neutralized magnesium oxide powder and modified polymer polyvinyl acetate. It can be directly used for road construction; after diluent is added, it is directly used for waterproofing and corrosion protection of the outer layer of pipelines. Not afraid of high temperature, freezing, not afraid of ultraviolet radiation, strong adhesion, long service life, easy to obtain materials, low cost, simple production, a wide market.
【技术实现步骤摘要】
一种防水防腐蚀涂料
本专利技术属于建筑业中防水防腐化工涂料。特别涉及管道外层防潮防腐的一种防水防腐蚀涂料。
技术介绍
现有的管道外层防腐剂,大部分是先刷一层土红色的防锈漆后,再刷一层油漆或沥青,时间一长,沥青裂口脱落,防锈漆起皮影响防护效果。
技术实现思路
本专利技术的目的是提供一种耐潮湿、耐腐蚀、无毒、长寿命的防水防腐蚀涂料。实现本专利技术的技术方案是:一种防水防腐蚀涂料,它包含沥青、顺酐、氧化镁及聚醋酸乙烯脂,其特征在于:它以70-100号的沥青为主要原料,在溶化的沥青液体中加入总体积2-7%的顺酐进行酸化处理1-2分钟,再加进总体积2-7%的氧化镁粉充分搅拌均匀,最后加入总体积0.5%的聚醋酸乙烯脂,经充分混合后,灌装到塑料桶内密封保存。所述的防水防腐蚀涂料作筑路材料时则直接使用;作管道防护层用时,还要加入汽油、溶剂油、碳酒三者之一作为稀释剂。本专利技术与现有技术相比:其优点是普通沥青经过顺酐酸化和氧化镁中和处理后,再加入高分子材料聚醋酸乙烯脂,对沥青进行改性,使其高温日晒不变软,寒冬酷冷不裂口,不怕紫外线照射而老化,所铺路面寿命长。用于管道防腐蚀只需加稀剂后直接刷涂,省去了先刷防腐漆的工序,既省料又省时,无毒、无味、无环境污染,同时粘着力强、耐寒不裂口,因此增加管线几倍的使用寿命。因质优价低,寿命长而市场广大。下面结合最佳实施例对本专利技术予以说明。实施例1.本专利技术是以70-100号的沥青为主要原料,先将沥青溶化成液体,然后加入总体积的5%的顺酸酐进行酸化处理,1-2分钟后加入总体积5%的氧化镁粉中和后,再加入总体积0.5%的高分子材料聚醋酸乙烯脂 ...
【技术保护点】
1.一种防水防腐蚀涂料,它包含沥青、顺酐、氧化镁及聚醋酸乙烯脂, 其特征在于:它以70‑100号的沥青为主要原料,在溶化的沥青液体中加入总体 积2‑7%的顺酐进行酸化处理1‑2分钟,再加进总体积2‑7%的氧化镁粉充分搅 拌均匀,最后加入总体积0.5%的聚醋酸乙烯脂,经充分混合后,灌装到塑料桶 内密封保存。
【技术特征摘要】
1.一种防水防腐蚀涂料,它包含沥青、顺酐、氧化镁及聚醋酸乙烯脂,其特征在于:它以70-100号的沥青为主要原料,在溶化的沥青液体中加入总体积2-7%的顺酐进行酸化处理1-2分钟,再加进总体积2-7%的氧化镁粉充分搅拌均匀,最后加入...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。