The invention is an elastic acrylate golf course coating, which is copolymerization emulsion of butyl acrylate 40 to 70%, methyl methacrylate 5 to 40%, styrene 0 - 20% and N-hydroxymethyl acrylamide 1 - 15% by emulsion polymerization. The coating is made up of 40-60 parts of the emulsion, 60-40 parts of solid material and 0. 1% dispersant. Solid material is composed of cement 40% - 100% and body filler 0 - 60%. The coating of the invention has moderate elasticity, good texture, excellent ultraviolet resistance, is not easy to ageing, and does not need regular maintenance. Long service life, low price, innocuity and tasteless, simple construction. The product is used for golf course coating.
【技术实现步骤摘要】
一种弹性丙烯酸酯球场涂料
本专利技术涉及高分子乳液聚合与涂料领域,特别是涉及一种弹性丙烯酸酯球场涂料。
技术介绍
过去所用球场涂料是刚性丙烯酸酯涂料或聚氨酯涂料,优点是无需经常保养,缺点是雨后不能马上恢复使用,2-3年需维护,弹性一般,因此,人们一直寻找较好的球场涂料,以解决市场急需问题。
技术实现思路
本专利技术的目的在于克服上述现有技术中的不足之处,而提供一种弹性丙烯酸酯球场涂料。本专利技术通过如下措施来实现的:本专利技术采用乳液聚合法,将丙烯酸丁酯40-70%,甲基丙烯酸甲酯5-40%,苯乙烯0-20%和N-羟甲基丙烯酰胺单体1-15%,在0.2-2%的表面活性剂和0.1-1%的引发剂的作用下,在水中共聚合,生成固含量为50-56%的乳液。表面活性剂可为阴离子型或非离子型或两者的混合型。引发剂可为过硫酸盐或过氧化物。由水泥40-100%,体质填料0-60%混合而成固体料。体质填料可为方解石、碳酸钙、滑石粉、二氧化硅、硫酸钡、磁土等。涂料按重量份的配比和原料所组成,由乳液40-60份,固体料60-40份及0.1-1份的分散剂组成。分散剂可为三聚磷酸钾、焦磷酸盐、六偏磷酸盐等。在找平的球场基面上涂上两层涂料:下面为弹性层,厚度2~4毫米;上面为耐磨面层,面层厚度为0.4~1毫米。在面层中加入所需颜色的色浆,可得到令人满意的效果。本专利技术与现有技术相比具有如下优点:本专利技术的乳液能与水泥有较好的交联,使涂料具有高强度、高拉伸和高弹性,并具有优异的耐候性及耐化性能,价格低,使用寿命长,无毒无味,施工简单。本专利技术的球场涂料与传统的球场涂料相比具有明显的优越 ...
【技术保护点】
1.一种弹性丙烯酸酯球场涂料,其特征在于它是按重量份 配比和原料制成,乳液40‑60份,固体料60‑40份及0.1‑1 份的分散剂,其中乳液是用乳液聚合法,将丙烯酸丁酯40‑70 %,甲基丙烯酸甲酯5‑40%,苯乙烯0‑20%和N‑羟甲基丙 烯酰胺单体1‑15%,在0.2‑2%的表面活性剂和0.1‑1%的 引发剂的存在下,水中共聚合,生成固含量为50‑56%的乳液, 固体料由水泥40‑100%,体质填料0‑60%混合而成。
【技术特征摘要】
1.一种弹性丙烯酸酯球场涂料,其特征在于它是按重量份配比和原料制成,乳液40-60份,固体料60-40份及0.1-1份的分散剂,其中乳液是用乳液聚合法,将丙烯酸丁酯40-70%,甲基丙烯酸甲酯5-40%,苯...