The invention discloses a special compatibilizer and alloy for improving the mechanical properties of glass fiber reinforced PC/ABS alloy; the compatibilizer is a graft of polycarbonate with styrene, acrylonitrile and maleic anhydride terpolymer, namely PC_g_SAM, and the glass fiber reinforced PC/ABS alloy with excellent mechanical properties has the following weight parts. The compositions of PC: 30wt%~80wt%, ABS: 10wt%~50wt%, glass fiber: 5wt%~40wt%, compatibilizer: 1wt%~10wt%, antioxidant: 0.1wt%~1wt%, other additives: 0.1wt%~wt5%. Compared with the prior art, the invention provides a special compatibilizer for glass fiber reinforced PC/ABS alloy, and can greatly improve the mechanical properties of glass fiber reinforced PC/ABS composite material, and the process is simple and convenient for industrialization.
【技术实现步骤摘要】
用于PC/ABS合金的相容剂及PC/ABS合金
本专利技术涉及一种改善玻纤增强PC/ABS合金机械性能的专用相容剂及合金，属于高分子复合材料领域。
技术介绍
以PC和ABS为主要原料的PC/ABS合金是一种重要的工程塑料合金，其具有良好的成型性和耐低温冲击性能、较高的热变形温度及光稳定性。与PC相比，降低了熔体粘度，改善了加工性能，并大大提高了产品耐应力开裂的性能；与ABS相比，提高了耐热性和耐候性，兼具两者的良好性能。而玻纤增强的PC/ABS合金，其力学性能更优异，在电子、电器以及汽车等诸多领域得到广泛的应用。随着社会发展，工业技术的革新，电子、电器特别是汽车行业对玻纤增强PC/ABS合金的需求也越来越大。由于其具有优异的机械性能，所以被广泛用于手机外壳、计算机和商业机器壳体、电器设备、汽车零件仪表板、内部装修以及车轮盖，还有高速铁路车辆内阻燃装饰板及电器部件机械零配件、电子电器组件等。虽然玻纤增强PC/ABS的机械性能十分优异，但是在加工成型过程中容易出现玻纤与树脂混合不匀、成型困难、浮纤、制品表面毛糙、光泽度降低等问题。目前，市面上通常使用PE接枝类、ABS...
【技术保护点】
1.一种用于PC/ABS合金的相容剂，其特征在于，包括按重量百分数计的如下反应组分：PC树脂： 70～95％；SAM树脂： 5～30％。
【技术特征摘要】
1.一种用于PC/ABS合金的相容剂，其特征在于，包括按重量百分数计的如下反应组分：PC树脂：70～95％；SAM树脂：5～30％。2.如权利要求1所述的用于PC/ABS合金的相容剂，其特征在于，所述PC树脂的数均分子量为10000～40000g/mol，玻璃化温度为140～150℃。3.如权利要求1所述的用于PC/ABS合金的相容剂，其特征在于，所述SAM树脂中，MAH的含量为2～25wt％。4.一种如权利要求1所述的用于PC/ABS合金的相容剂的制备方法，其特征在于，包括如下步骤：将PC树脂和SAM树脂混匀后，投入双螺杆挤出机，经熔融挤出、造粒，得到所述相容剂。5.如权利要求4所述的用于PC/ABS合金的相容剂的制备方法，其特征在于，所述双螺杆挤出机的挤出温度为200～280℃，主机转速为180～600rpm。6.一种PC/ABS合金组合物，其特征在于，包...
【专利技术属性】
技术研发人员：李心良，汤俊杰，史鹏伟，金光润，
申请(专利权)人：佳易容相容剂江苏有限公司，
类型：发明
国别省市：江苏,32