The invention discloses a preparation method of Fly Ash Sludge ceramsite, the technical field of fly ash recycling and sludge waste utilization. The raw material of ceramsite is composed of 30-60% fly ash, 30-60% water plant sludge, 3-9% paper mill sludge and 0-10% sewage plant sludge. The raw materials were mixed with water in a certain proportion to form pellets. The temperature was raised to 1100 ~1200 C by several stages and maintained for 15 minutes at this temperature. The sintered ceramsite had larger and denser voids, lower water absorption, smoother interior, compact structure and higher natural strength, which accorded with the standard of using ceramsite for building materials.
【技术实现步骤摘要】
一种粉煤灰污泥陶粒的制备方法
本专利技术涉及粉煤灰回收利用，污泥废物利用
，尤其涉及一种粉煤灰污泥陶粒的制备方法。
技术介绍
粉煤灰是电厂锅炉所产生的灰渣。其中煤粉锅炉为悬浮燃烧，煤粉在燃烧后残余的灰渣大部分是极细小的球形玻璃体，它随着烟气离开炉膛成为飞灰，经收尘器收集后排放，这就是粉煤灰。近年来，随着国家对环境保护工作的日益重视，政府部门对企业的环保工作也有明确的要求，在此背景下，有关生产企业中如何使粉煤灰变废为宝，减少环境污染，进而达到提高经济效益和发展循环经济的目的，亦已成为迄今包括建材企业在内的众多生产企业致力研究的主要技术课题。污泥是一种由有机残片、细菌体、无机颗粒和胶体等组成的非均质体。它很难通过沉降进行彻底的固液分离。污泥成分极其复杂，如不加任何处理，不仅会占用大量的土地，还会造成二次污染，尤其是对土壤和地下水的污染，目前污泥的处理处置手段主要有污泥填埋、污泥农用、污泥焚烧、污泥的堆肥化处理技术、污泥的燃料化技术、污泥的厌氧消化技术等，这些技术虽然也使一部分污泥得到有效的控制与治理，但处理效果并不是很好，而且耗费大量的人力以及财力，污泥也并不能...
【技术保护点】
1.一种粉煤灰污泥陶粒的制备方法，其特征在于，包括以下步骤：(1)将粉煤灰和污泥分别干燥至恒重、研磨成粉过40目筛；(2)将粉煤灰和污泥混合均匀得到陶粒原料；(3)将步骤(2)所得陶粒原料放入造粒机内，并加入5％的水，使原料润湿；(4)启动造粒机并将转速提高至1400r/min，在该转速下转动10min，降低转速至500r/min并在20min内加水至原料含水15％，然后再将造粒机的转速提高至1400r/min并保持转动5～10min，可得生料球；(5)将步骤(4)所得生料球送入电阻炉内，以10℃/min的速率升温至500℃并恒温10min，然后降温至100℃并恒温5min...
【技术特征摘要】
1.一种粉煤灰污泥陶粒的制备方法，其特征在于，包括以下步骤：(1)将粉煤灰和污泥分别干燥至恒重、研磨成粉过40目筛；(2)将粉煤灰和污泥混合均匀得到陶粒原料；(3)将步骤(2)所得陶粒原料放入造粒机内，并加入5％的水，使原料润湿；(4)启动造粒机并将转速提高至1400r/min，在该转速下转动10min，降低转速至500r/min并在20min内加水至原料含水15％，然后再将造粒机的转速提高至1400r/min并保持转动5～10min，可得生料球；(5)将步骤(4...
【专利技术属性】
技术研发人员：吴代赦，李亚静，李建龙，杜俊逸，吴泉泉，
申请(专利权)人：南昌大学，
类型：发明
国别省市：江西,36