用于生物油加氢脱氧反应的Ni2P/还原氧化石墨烯催化剂及其制备方法技术

本发明专利技术公开了一种用于生物油加氢脱氧反应的Ni2P/还原氧化石墨烯催化剂及其制备方法，该催化剂是以还原氧化石墨烯为载体，负载活性组分Ni2P，以催化剂计，Ni2P的负载量为10％～25％。本发明专利技术催化剂制备条件相对温和，其用于苯甲醛加氢脱氧制备甲苯的反应体系中，苯甲醛转化率最高可达96％以上，对甲苯的选择性接近90％，催化剂活性好，选择性高，并且稳定性强，成本远低于贵金属催化剂，具有非常显著的应用价值。

Ni2P/ reduced graphene oxide catalyst for hydrodeoxygenation of bio oil and preparation method thereof

The invention discloses a Ni2P/reduced graphene oxide catalyst for bio-oil hydrodeoxygenation reaction and a preparation method thereof. The catalyst is supported on reduced graphene oxide and loaded with active component Ni2P. The supported amount of Ni2P is 10%~25% by catalyst. The preparation condition of the catalyst is relatively mild. In the reaction system used for the hydrogenation and deoxidation of benzaldehyde to toluene, the conversion of benzaldehyde can be up to 96%, the selectivity of p-toluene is close to 90%, the catalyst has good activity, high selectivity, strong stability, and the cost is far lower than that of noble metal catalyst. Application value.

【技术实现步骤摘要】
用于生物油加氢脱氧反应的Ni2P/还原氧化石墨烯催化剂及其制备方法
本专利技术属于催化加氢
，具体涉及一种用于生物油加氢脱氧反应的Ni2P/还原氧化石墨烯催化剂，以及该催化剂的制备方法。
技术介绍
生物油加氢脱氧反应是其加氢精制过程的手段。按照加氢的程度不同，其也可分为深度加氢脱氧和轻度加氢脱氧两种类型。按照加氢条件的不同，加氢脱氧可分为两种类型，通过热处理实现的过程称为热加氢脱氧，通过催化剂作用实现的过程称为催化加氢脱氧。但是，采用热加氢脱氧方式得到的产物，脱氧率不太理想，一般为78％～85％。相比之下，由于催化加氢脱氧催化剂的加入，使得其脱氧过程条件相对温和，且脱氧率极高。磷化物具有特殊电子层结构和良好的催化性能，是用于生物油加氢脱氧的理想型催化剂之一，但是磷化物在高温下对水的敏感度较高，易于形成无催化性能、能还原的磷酸盐类物质(李克伦.负载磷化物催化剂苯甲醚加氢脱氧性能研究[D].天津:天津大学,2012)；由于Ni2P比表面积很小(不超过14m2/g)，将其负载到载体上能显著提高催化剂活性相的分散。Al2O3刚性强，廉价易得，在工业催化剂中得到广泛应用(SawhillS本文档来自技高网...

【技术保护点】
1.一种用于生物油加氢脱氧反应的Ni2P/还原氧化石墨烯催化剂，其特征在于：该催化剂是以还原氧化石墨烯为载体，负载活性组分Ni2P，以催化剂计，Ni2P的负载量为10％～25％。

【技术特征摘要】
1.一种用于生物油加氢脱氧反应的Ni2P/还原氧化石墨烯催化剂，其特征在于：该催化剂是以还原氧化石墨烯为载体，负载活性组分Ni2P，以催化剂计，Ni2P的负载量为10％～25％。2.根据权利要求1所述的催化剂，其特征在于：以催化剂计，Ni2P的负载量为15％～20％。3.一种权利要求1所述的催化剂的制备方法，其特征在于：以催化剂计，按照Ni2P的负载量为10％～25％，且Ni元素和P元素的摩尔比为2:1.5，将氧化石墨烯超声分散于NaH2PO2·H2O和NiCl2·...

【专利技术属性】
技术研发人员：徐海升，王豪，丁丽芹，
申请(专利权)人：西安石油大学，
类型：发明
国别省市：陕西,61