The invention relates to a cordierite bonded calcium aluminate casket and a preparation method thereof. The technical scheme is as follows: firstly, the raw material is mixed with 50-65wt% calcium hexaaluminate aggregate, 25-35wt% cordierite powder and 5-15wt% plastic clay, and then the binder with 4-8wt% of the raw material is added, which is evenly mixed, pressed and dried, and then heated for 8-10h at 1350-1400 C, the cordierite binder is obtained. Calcium aluminate casket. The invention has the characteristics of low production cost and simple preparation process, and the cordierite bonded calcium hexaaluminate sagger has excellent corrosion resistance and long service life.
【技术实现步骤摘要】
一种堇青石结合六铝酸钙匣钵及其制备方法
本专利技术属于匣钵
特别涉及一种堇青石结合六铝酸钙匣钵及其制备方法。
技术介绍
高温固相合成法因工艺简单以及对设备要求低，在锂离子电池正极材料的实际生产中得到了广泛应用，匣钵作为高温焙烧过程中盛装原料的容器，主要因合成正极原料的侵蚀和反复的冷热循环出现损毁。随着锂离子电池行业的快速发展，锂离子电池日益增长的需求量和高电压的发展趋势对匣钵的性能提出了更为严格的要求。“锆莫来石匣钵”(ZL201410189300.9)专利技术，公开了一种以莫来石、板状刚玉和锆英砂等为原料制备匣钵的方法，该技术采用的原料具有良好的热震稳定性，但原料价格昂贵和烧成温度高，不利于大规模生产。“循环式锂电池正极材料用焙烧匣钵及其制备方法”(ZL201310194571.9)专利技术，分别以莫来石和氧化锆等原料制得匣钵基体层和工作层，匣钵的抗侵蚀性能得到提高，但基体层与工作层间的结合部位在使用过程中易开裂。“一种抗锂电池高温腐蚀层状匣钵及其制备方法”(CN201610159994.0)专利技术，公开了一种底面具有三层结构的匣钵的制备方法，成型步骤...
【技术保护点】
1.一种堇青石结合六铝酸钙匣钵的制备方法，其特征在于所述制备方法是：先以50～65wt％的六铝酸钙骨料、25～35wt％的堇青石粉料和5～15wt％的塑性黏土为原料混合，再外加所述原料4～8wt％的结合剂，混合均匀，机压成型，干燥，然后在1350～1400℃条件下保温8～10h，制得堇青石结合六铝酸钙匣钵。
【技术特征摘要】
1.一种堇青石结合六铝酸钙匣钵的制备方法，其特征在于所述制备方法是：先以50～65wt％的六铝酸钙骨料、25～35wt％的堇青石粉料和5～15wt％的塑性黏土为原料混合，再外加所述原料4～8wt％的结合剂，混合均匀，机压成型，干燥，然后在1350～1400℃条件下保温8～10h，制得堇青石结合六铝酸钙匣钵。2.根据权利要求1所述的堇青石结合六铝酸钙匣钵的制备方法，其特征在于所述六铝酸钙的主要化学成分是：Al2O3≥90wt％，CaO≥7.5wt％；六铝酸钙的体积密度≥2.8g/cm3，显气孔率≤13％；六铝酸钙骨料的颗粒级配是：粒径小于2mm且大于等于1mm的为20～30wt％，粒径小于1mm且大于等于...
【专利技术属性】
技术研发人员：向若飞，李远兵，李淑静，欧阳思，罗瀚，李仕祺，
申请(专利权)人：武汉科技大学，
类型：发明
国别省市：湖北,42