The utility model relates to a baking free ceramic sawdust board (porcelain board), which relates to the technical field of plates. The unburned ceramic wood chips board is made of the following components: 100 unburned ceramics, 5-25 wood chips and 0-160 sand. The unburned ceramics are made by adding 0.1 to 10 parts of porcelain into 100 portions of cement, and the wood chips are plant chips. The burning-free ceramic wood chips board can be sawed and nailed, and is light in weight, environmentally friendly, fire-proof, insect-proof, water-proof, mildew-proof, acid and alkali-proof, non-toxic, tasteless, non-irritating, non-corrosive metal, anti-aging for more than 50 years, and has the advantages of low cost, easy access to raw materials for manufacture, and can be widely used in the fields of construction, furniture and decoration. Surface, wall, skeleton, floor, roof, furniture, toilet, piping, doors and windows, etc.
【技术实现步骤摘要】
一种免烧陶瓷木屑板（瓷木板）
本专利技术涉及板材领域，具体涉及一种免烧陶瓷木屑板。
技术介绍
目前在建筑、家具、装饰等行业中广泛使用的板材主要有木板、硅钙板、石膏板、镁基板、石塑板、木塑板、中纤板、水泥纤维板、稻草板、桔杆板等等，这些板材各有各的不足之处。例如，木板成本高、不耐久，硅钙板成本高、难清洗、防潮性能差，石膏板容易粉状碎裂，玻镁板容易泛霜起白、耐水性差、对钢材有一定的腐蚀性，木塑板材料质地较脆、韧性不够、抗撞击性不强，中纤板不防潮、遇水膨胀率大、变形大。另外，也有不少厂家使用水泥混合木屑来生产水泥木屑板，但是目前这种水泥木屑板也存在有难以克服的缺点：由于木屑属于酸性物质，而水泥属于碱性物质，两者“合不来”，如果使用现有水泥来混合木屑制作水泥木屑板的话，木屑会慢慢释放出酸性物质来破坏水泥的强度，甚至使水泥粉化，致使水泥木屑板质量不好、强度不高、使用寿命不长，因此其在市场上一直无法推开、无法得到广泛应用。
技术实现思路
本专利技术的目的在于克服现有板材的上述不足，提供一种能够像木板一样可钉、可锯，而且质轻、长寿命、低成本的板材。本专利技术免烧陶瓷木屑板由包括以下...
【技术保护点】
1.一种免烧陶瓷木屑板，其特征是，免烧陶瓷木屑板由包括以下质量份数组分的原料加网筋制成：免烧陶瓷100份，木屑5～25份，砂子0～160份；将上述原料混合后加入25～75份水，搅拌后制成板状；在制板过程中将网筋铺垫到板体中，在免烧陶瓷硬化后做成免烧陶瓷木屑板。
【技术特征摘要】
1.一种免烧陶瓷木屑板，其特征是，免烧陶瓷木屑板由包括以下质量份数组分的原料加网筋制成：免烧陶瓷100份，木屑5～25份，砂子0～160份；将上述原料混合后加入25～75份水，搅拌...
【专利技术属性】
技术研发人员：陈艺通，
申请(专利权)人：广州市轻能建材有限公司，
类型：发明
国别省市：广东,44