The invention discloses a method for connecting HIT solar cells and a HIT photovoltaic module, which relates to the technical field of solar cells, and is designed to reduce the manufacturing cost of HIT photovoltaic modules and the packaging efficiency loss of HIT photovoltaic modules. The connecting method of the HIT solar cell sheet includes: preheating a plurality of HIT solar cell sheets to be connected in series; welding a plurality of HIT solar cell sheets to be connected in series with a welding belt to produce a series of HIT solar cells, wherein the welding temperature is 150 ~190 ~C; and connecting the HIT solar cell sheets in series and parallel. The invention is used to improve the performance of HIT photovoltaic modules.
【技术实现步骤摘要】
一种HIT太阳能电池片的连接方法及HIT光伏组件
本专利技术涉及太阳能组件
，尤其涉及一种HIT太阳能电池片的连接方法及HIT光伏组件。
技术介绍
三洋公司专利技术了HIT(HeterojunctionwithintrinsicThinlayer)太阳能电池片，所谓HIT太阳能电池片就是一种利用晶体硅基板和非晶硅薄膜制成的混合型太阳能电池，其结构中具有非掺杂即本征的非晶硅薄膜层结构。HIT太阳能电池片具有转换效率高、稳定性好的特点。HIT光伏组件需要在低温工艺下封装，对温度要求比较严格，所以，目前HIT光伏组件中的HIT电池片在串联时，采用导电胶粘结工艺，在生产线上无法采用现有的太阳能电池组件的焊接设备，就需要定制专用的粘结设备，导致制造成本高，且导电胶自身具有较大的电阻，增加了封装效率损失，最终降低HIT光伏组件的功率。
技术实现思路
本专利技术的实施例提供一种HIT太阳能电池串的串联方法及HIT光伏组件，焊带焊接工艺替换了现有的导电胶粘结工艺，采用现有的焊接设备就可实现焊带的焊接，且焊带相比导电胶电阻小，降低了封装效率损失，提高了HIT光伏组件的功率。为达到...
【技术保护点】
1.一种HIT太阳能电池片的连接方法，其特征在于，包括以下步骤：对多个待串联HIT电池片预热；采用焊带对所述多个待串联HIT电池片串联焊接，以制得HIT太阳能电池串，其中，所述焊接温度为150℃～190℃；将所述HIT太阳能电池串并联焊接。
【技术特征摘要】
1.一种HIT太阳能电池片的连接方法，其特征在于，包括以下步骤：对多个待串联HIT电池片预热；采用焊带对所述多个待串联HIT电池片串联焊接，以制得HIT太阳能电池串，其中，所述焊接温度为150℃～190℃；将所述HIT太阳能电池串并联焊接。2.根据权利要求1所述的HIT太阳能电池片的连接方法，其特征在于，对所述多个待串联HIT电池片串联焊接时，采用电镀工艺制备的焊带进行焊接。3.根据权利要求1所述的HIT太阳能电池片的连接方法，其特征在于，相串联焊接的所述待串联HIT电池片以叠瓦方式首尾重叠。4.一种HIT光伏组件，其特征在于，包括：使用如权利要求1-3任一所述的HIT太阳能电池片的连接方法制得的HIT太阳能电池组件，和两个相对设置的封装板，所述HIT太阳能电池组件夹设在两个所述封装板之间，所述HIT太阳能电...