The invention discloses a ceramic cutting knife for large-scale paper cutting. The ceramic cutting knife is made of the following ceramic materials. The ceramic materials include the following weight components: lanthanum oxide 4_9 phr, silane coupling agent 4_6 phr, anhydrous carbonate 6_10 phr, dolomite 7_9 phr, borax 8_13 phr, butyl terephthalate 1 phr. 5, 9 13 carbon fibers, 7 10 glass fibers, 7 9 octylphenol polyoxyethylene ether, 5 10 polyethylene glycol, 15 24 chromium carbide powder, 5 7 hydroxyethyl cellulose, 8 11 magnesium oxide, 5 7 boron nitride, 6 9 aluminum nitride, 7 10 titanium oxide, 15 20 ferric oxide, 9 9 zirconia, 13 dioxide Silicon 35 to 40, diatomite 6, 8, ethyl acetate 6, 8, manganese 10, 14. The invention has good strength and hardness, good oxidation resistance and good toughness, and has wide adaptability.
【技术实现步骤摘要】
一种大规模切纸用的陶瓷切割刀
本专利技术是属于陶瓷切割刀
，具体说是一种大规模切纸用的陶瓷切割刀。
技术介绍
近年来陶瓷切割刀品类繁多，根据需求进行了一次次的改进，现有的陶瓷切割刀具有强度高，往往是单纯追求强度高，而忽略了耐氧化性能和韧性的提高。
技术实现思路
为解决现有技术中的问题，本专利技术专利目的是提供一种大规模切纸用的陶瓷切割刀。为达到上述目的，本专利技术采用的技术方案是：一种大规模切纸用的陶瓷切割刀，所述陶瓷切割刀采用如下陶瓷材料加工而成，该陶瓷材料包括以下重量份的组分：氧化镧4-9份，硅烷偶联剂4-6份，无水碳酸里6-10份，白云石7-9份，硼砂8-13份，太酸丁酯份1-5，碳纤维9-13份，玻璃纤维7-10份，辛基酚聚氧乙烯醚7-9份，聚乙二醇5-10份，碳化铬粉15-24份，羟乙基纤维素份5-7，氧化镁8-11份，氮化硼份5-7，氮化铝6-9份，氧化钛7-10份，氧化铁15-20份，二氧化锆9-13份，二氧化硅35-40份，硅藻土6-8份，乙酸乙酯6-8份，锰10-14份。本专利技术具有以下优点：1、本专利技术具有极高的强度和硬度，耐氧化，同时具有一定韧性；适应性非常广泛。具体实施方式下面结合具体实施例对专利技术作进一步说明。实施例1一种大规模切纸用的陶瓷切割刀，所述陶瓷切割刀采用如下陶瓷材料加工而成，该陶瓷材料包括以下重量份的组分：氧化镧4-9份，硅烷偶联剂4-6份，无水碳酸里6-10份，白云石7-9份，硼砂8-13份，太酸丁酯份1-5，碳纤维9-13份，玻璃纤维7-10份，辛基酚聚氧乙烯醚7-9份，聚乙二醇5-10份，碳化铬粉15-2...
【技术保护点】
1.一种大规模切纸用的陶瓷切割刀，其特征在于：所述陶瓷切割刀采用如下陶瓷材料加工而成，该陶瓷材料包括以下重量份的组分：氧化镧4‑9份，硅烷偶联剂4‑6份，无水碳酸里6‑10份，白云石7‑9份，硼砂8‑13份，太酸丁酯份1‑5，碳纤维9‑13份，玻璃纤维7‑10份，辛基酚聚氧乙烯醚7‑9份，聚乙二醇5‑10份，碳化铬粉15‑24份，羟乙基纤维素份5‑7，氧化镁8‑11份，氮化硼份5‑7，氮化铝6‑9份，氧化钛7‑10份，氧化铁15‑20份，二氧化锆9‑13份，二氧化硅35‑40份，硅藻土6‑8份，乙酸乙酯6‑8份，锰10‑14份。
【技术特征摘要】
1.一种大规模切纸用的陶瓷切割刀，其特征在于：所述陶瓷切割刀采用如下陶瓷材料加工而成，该陶瓷材料包括以下重量份的组分：氧化镧4-9份，硅烷偶联剂4-6份，无水碳酸里6-10份，白云石7-9份，硼砂8-13份，太酸丁酯份1-5，碳纤维9-13份，玻璃纤维7-10份，辛...