The invention relates to a method for preparing graphene/palladium nanocatalyst by photoreduction of phosphotungstic acid. The steps are as follows: firstly, the solution containing phosphotungstic acid and isopropanol is mixed with graphene oxide by ultrasonic wave; secondly, the solution of chloropalladium acid is mixed with the mixture by ultrasonic wave, and the solution is irradiated by ultraviolet lamp after mixing. Catalysts for direct alcohol fuel cells. The method of the present invention is to obtain graphene/palladium nanocatalyst by utilizing ultraviolet light to provide energy so that phosphotungstic acid has the ability of reducing. The method is simple and easy to operate, and the obtained catalyst has good catalytic activity for alcohols, and can be widely used in direct alcohol fuel cells.
【技术实现步骤摘要】
一种利用磷钨酸光还原制备石墨烯/钯纳米催化剂的方法
本专利技术涉及燃料电池电催化剂
，特别是涉及一种利用磷钨酸光还原制备石墨烯/钯纳米催化剂的方法。
技术介绍
石墨烯是一种二维碳材料，具有较高的比表面积、良好的导电性和热稳定性能，在电池、电子器件、传感器及材料方面得到广泛应用。氧化石墨烯是石墨烯的氧化物，氧化石墨烯上含氧官能团增多而使其性质比石墨烯更加活泼。采用石墨烯负载型催化剂可大大降低贵金属钯的负载量，同时提高其利用率，提高其催化活性。通过一步制备石墨烯/钯纳米催化剂，避免引入其他杂质。
技术实现思路
本专利技术的目的在于提供一种利用磷钨酸光还原制备石墨烯/钯纳米催化剂的方法，本专利技术提供的方法步骤简单，且得到的催化剂具有良好的催化活性。一种利用磷钨酸光还原制备石墨烯/钯纳米催化剂的方法，具体步骤如下：A)将磷钨酸、异丙醇混合液与氧化石墨烯溶液进行超声，得到三者的混合液；B)将所述步骤A)得到的混合液和氯钯酸溶液超声混合，混合后置于紫外灯下照射；C)将所述步骤B)得到的混合液离心，离心后得到产物进行电化学测试。优选的，所述步骤A中配制磷钨酸与异丙醇混合液所...
【技术保护点】
1.一种利用磷钨酸光还原制备石墨烯/钯纳米催化剂的方法，其特征在于，包括步骤：A)将磷钨酸、异丙醇混合液与氧化石墨烯溶液混合超声，得到三者的混合液；B)将所述步骤A)得到的混合液和氯钯酸溶液超声混合，混合后置于紫外灯下照射，得到所述直接醇类燃料电池电催化剂。C)将所述步骤B)得到的混合液离心，离心后得到产物进行电化学测试。
【技术特征摘要】
1.一种利用磷钨酸光还原制备石墨烯/钯纳米催化剂的方法，其特征在于，包括步骤：A)将磷钨酸、异丙醇混合液与氧化石墨烯溶液混合超声，得到三者的混合液；B)将所述步骤A)得到的混合液和氯钯酸溶液超声混合，混合后置于紫外灯下照射，得到所述直接醇类燃料电池电催化剂。C)将所述步骤B)得到的混合液离心，离心后得到产物进行电化学测试。2.根据权利要求1所述的制备方法，其特征在于，所述步骤A中配制磷钨酸与异丙醇混合液所需的水为电阻率不小于18.2MΩ·cm的超纯水。3.根据权利要求1所述的制备方法，其特征在于，所述步骤A中超声混合的时间为10min～20min，反应条件为室温。4.根据权利要求1所述的制备方法，其特征在于，所述步骤B中氧化石墨烯与氯钯酸的质量比为1：(0.4～1)。5.根据权利...
【专利技术属性】
技术研发人员：刘哲林，赵博，胡婧，
申请(专利权)人：长春理工大学，
类型：发明
国别省市：吉林,22
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。